Fe510C2KI hlau

Txoj kev deoxidation FN = rimming steels tsis tso cai
Rau cov khoom siv ntev, P  thiab S cov ntsiab lus tuaj yeem siab dua 0.005%.
Cov hlau tuaj yeem qhia Ni cov ntsiab lus ntawm max. 0.65%
Nws tso cai kom dhau qhov ntsuas qhov ntsuas tau muab rau txhua qhov nce ntawm 0,001 % N tus P max. cov ntsiab lus yuav raug txo los ntawm 0,005%; N cov ntsiab lus ntawm lub ladle tsom xam, txawm li cas los xij, yuav tsum tsis txhob ntau tshaj 0,012%
Cov hlau yuav muaj max. 0.30% Mo thiab max. 0,15% yog '
Qhov max. tus nqi rau nitrogen tsis siv yog tias cov tshuaj muaj pes tsawg leeg qhia tau hais tias qhov tsawg kawg nkaus Al ntsiab lus ntawm 0,020% lossis yog tias muaj lwm yam N khi cov ntsiab lus txaus

C	Si	Mn	P	S	Cr	N	Cu	CEV
max 0.16	max 0.5 hli	0.5 - 1.5	max 0.035	max 0.035	0.4 - 0.8	max 0.009	0.25 - 0.55	max 0.52

Mechanical zog ntawm steel Fe510C2KI Steel

Nominal thickness (hli):	rau 3	3 - 100	100 - 150
Rm - Tensile zog (MPa)	510-680	470-630	450-600

Nominal thickness (hli):	rau 16	16 - 40	40 - 63	63 - 80	80 - 100	100 - 150
ReH - Yam tsawg kawg nkaus tawm lub zog (MPa)	355	345	335	325	315	295

KV - Impact zog (J) longitud.,	-20 ° 27	0 ° 27

Nominal thickness (hli):	1.5 - 2	2 - 2.5	2.5 - 3
A—Min. elongation Lo = 80 hli (%)	16	17	18

Nominal thickness (hli):	3 - 40	40 - 63	63 - 100	100 - 150
A—Min. elongation Lo = 5,65 √ Yog li (%)	22	21	20	18