ASTM A517

Spesifikasi ASTM A517 yaiku Spesifikasi Standar kanggo Plate Vessel Tekanan, Baja Paduan, Bahan Kekuwatan Dhuwur, Quenched lan Tempered sing digunakake ing aplikasi boiler las fusi lan kapal tekanan. Ing spesifikasi iki, kekandelan piring nemtokake pilihan kelas lan sifat mekanik. Piring 2,5" ing kekandelan lan ngisor, bakal duwe kekuatan Ngasilake minimal 100 ksi.  Piring liwat 2,5" ing kekandelan bakal duwe kekuatan Ngasilake minimal 90 ksi. Aplikasi khas kalebu prau lan tank sing ora dipecat.

Teknologi Tambahan:   Tes HIC | NACE MR0175 | Z15 | Z25 | Z35 | S1 | S2 | S3 | S5 | S6 | S7 | S8 | S9 | S11 | S12 | S17.

Ketebalan: 6-300 MM,
Jembar: 1500mm nganti 4050mm,
Dawane: 3000mm nganti 15000mm

Gnee steel khusus nyedhiyakake pelat baja ASTM A517. Kanggo informasi luwih lengkap babagan piring baja A517, priksa ing ngisor iki:

Plat baja ASTM A517 Grade A, A517 Gr.A, A517GrA

Spesifikasi standar ASTM A517 kanggo piring kapal tekanan, baja paduan, kekuatan dhuwur, dipateni lan tempered.
Baja kasebut kudu dipateni lan kudu cocog karo syarat ukuran butir austenitik sing apik saka Spesifikasi A20/A20M.

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S
A517 kelas A	0.13-0.23	0.34-0.86	0.74-1.20	0.035	0.035
	Cr	Mo	B	Zr
	0.46-0.84	0.15-0.31	0.0025	0.04-0.16

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade A Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas A	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

Plat baja ASTM A517 Grade B, A517 Gr.B, A517GrB

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S
A517 kelas B	0.13-0.23	0.13-0.37	0.64-1.10	0.035	0.035
	Cr	Mo	B	Ti	V
	0.36-0.69	0.12-0.28	0.0005-0.005	0.01-0.05	0.02-0.09

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade B Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas B	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

ASTM A517 Grade E,A517 Gr.E,A517GrE piring baja

Komposisi EChemical kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S
A517 kelas E	0.10-0.22	0.08-0.45	0.35-0.78	0.035	0.035
	Cr	Mo	B	Ti	V
	1.34-2.06	0.36-0.64	0.001-0.005	0.005-0.11

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade E Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas E	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

Plat baja ASTM A517 Grade F, A517 Gr.F, A517GrF

Komposisi kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S	Cu
A517 kelas F	0.08-0.22	0.13-0.37	0.55-1.10	0.035	0.035	0.12-0.53
	Cr	Mo	B	V	Ni
	0.36-0.69	0.36-0.64	0.0005-0.006	0.02-0.09	0.67-1.03

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade F Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas F	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

Plat baja ASTM A517 Grade H, A517 Gr.H, A517GrH

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S	Ni
A517 kelas H	0.10-0.23	0.13-0.37	0.87-1.41	0.035	0.035	0.27-0.73
	Cr	Mo	B	V
	0.36-0.69	0.17-0.33	MIN 0,0005	0.02-0.09

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade H Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas H	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

Plat baja ASTM A517 Grade P,A517 Gr.P,A517GrP

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S	Ni
A517 kelas P	0.10-0.23	0.18-0.37	0.40-0.78	0.035	0.035	1.15-1.55
	Cr	Mo	B
	0.79-1.26	0.41-0.64	0.001-0.005

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade P Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas P	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

ASTM A517 Grade Q, A517 Gr.Q, A517GrQ plat baja

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S	Ni
A517 kelas Q	0.12-0.23	0.13-0.37	0.87-1.41	0.035	0.035	1.15-1.55
	Cr	Mo	V
	0.94-1.56	0.36-0.64	0.02-0.09

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade Q Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas Q	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%

ASTM A517 Grade S,A517 Gr.S,A517GrS pelat baja

Komposisi Kimia kelas A517
sasmita	Elemen Maks (%)
	C	Si	Mn	P	S	Ti
A517 kelas S	0.10-0.22	0.13-0.45	1.02-1.62	0.035	0.035	0.07
	Cb	Mo
	0.07	0.10-0.38

Setara Karbon: Ceq = 【C+Mn/6+(Cr+Mo+V)/5+(Ni+Cu)/15】%

sasmita		A517 grade S Properti Mekanik
	kekandelan	ngasilaken	Tarik	Elongation
A517 kelas S	mm	Min Mpa	Mpa	Min %
	6-65	690	795-930	16%
	65-150	620	725-930	14%