S275JR lamina ferrea

EN 10025 S275 Steel (S275JR, S275J0 & S275J2)
EN 10025 S275 Ferro est gradus chalybi non-admixtum, secundum EN10025, S275 mitis chalybs in S275JR maxime dividitur (1.0044), S275J0 (1.0143) et S275J2 (1.0145). Quaedam proprietates S275 ferro leni melius est quam S235, et humilius quam S355.
S275 Materia designatio antiqua est St44 secundum vexillum Germaniae, qualis prior gradus aequipollens talis est;
EN10025 S275JR (1.0044) - St44-2 in DIN 17100
S275JO (1.0143) - St44-3U in DIN17100
S275J2 (1.0145) - S275J2G4 in EN 10025: 1993
EN10025 S275JR Definition (Designation)
Indices infra explicat EN10025 S275JR significatione
"S" est pro ferro structurali;
"275" refertur ad minimum cede roboris, quod 275 MPa crassitudine ferro probata est ≤ 16mm.
"JR" significat minimum valorem impulsum charpy in cella temperatura 27J.
"J0" refert ad valorem minimi pretii impulsum charpy in 0 °C 27J.
"J2" significat valorem minimum impulsum in -20 °C 27J.
S275 Data Sheet & Specification
EN 10025 S275 proprietatum ferri, compositionis et materiae aequipollens in sequenti notitia sheet inveniri potest. Data omnia charta DIN EN 10025-2 eadem est ac BS EN 10025-2 et in aliis membris EU civitatibus.

Catillus S275JR est lamina ferrea ex ferro leni vel carbo facta. Hae eæ ingentis usus habent ad structuram structuram, fabricandum in plantis, machinationibus, in fodiendis. Hae laminae ex S275JR mixturae factae sunt quae in natura valde versatiles sunt.

Compositio chemica
Datasheet I, EN10025 S275J0, S275J2 et S275JR compositio chemica in ladle analysi fundata in tabula sequenti datur.

			Compositio chemica (analysis capularum), %, ≤
Patria (Region)	Standard	Ferro Grade (Steel numerus)	C	Mn	P	S	N	Cu	Crassitudo (d) (mm).	Methodus deoxidationis
Unionem Europaeam	EN 10025-2	S275JR (1.0044)	0.21	1.50	0.035	0.035	0.012	0.55	≤ 40	Non licet ferro labris
			0.22						> 40
		S275J0 (1.0143)	0.18	1.50	0.030	0.030	0.012	0.55	≤ 150	Non licet ferro labris
			0.20						> 150
		S275J2 (1.0145)	0.18	1.50	0.025	0.025	-	0.55	≤ 150	plene occiditur
			0.20						> 150

Datasheet II, compositio chemica in analysi producti fundata.

			Compositio chemica (analysi producti), %, ≤
Patria (Region)	Standard	Ferro Grade (Steel numerus)	C	Mn	P	S	N	Cu	Crassitudo (d) (mm).	Methodus deoxidationis
Unionem Europaeam	EN10025-2	S275JR (1.0044)	0.24	1.60	0.045	0.045	0.014	0.60	≤ 40	Non licet ferro labris
			0.25						> 40
		S275Jo (1.0143)	0.21	1.60	0.040	0.040	0.014	0.60	≤ 150	Non licet ferro labris
			0.22						> 150
		S275J2 (1.0145)	0.21	1.60	0.035	0.035	-	0.60	≤ 150	plene occiditur
			0.22						> 150

S275 Steel Properties
Corporalia Properties
S275 densum mite chalybeum: 7.85 g/cm3
Puncta: 1420-1460 °F (2590-2660 °F)
Mechanica Properties
S275 Ferri proprietates mechanicae tales quae vires, distrahentes vires, elongationem et impulsum resistentiae cedunt, in notitia schedae infra dandae sunt.
Cedat imperium
Gradus S275 Datasheet - 3

		S275 Fortitudo cede (≥ MPa); Diae. (d) mm
Steel	Steel Grade (Steel Number)	d≤16	16< d ≤40	40< d ≤63	63< d ≤80	80< d ≤100	100< d ≤150	150< d ≤200	200< d ≤250
S275	S275JR (1.0044)	275	265	255	245	235	225	215	205
	S275J0 (1.0143)
	S275J2 (1.0145)

Distrahentes fortitudo
EN 10025 S275 Datasheet - 4

		S275 tensile fortitudo (≥ MPa)
Steel	Steel Gradus	d<3	3 ≤ d ≤ 100	100 < d ≤ 150	150 < d ≤ 250
S275	S275JR (1.0044)	430-580	410-560	400-540	380-540
	S275J0 (1.0143)
	S275J2 (1.0145)

Nota: 1MPa = 1N/mm2
Prolongatio
S275 materia Datasheet - 5

		Prolongatio (≥%); Crassitudo (d) mm
Steel	Steel Gradus	d≤1	1< d ≤1.5	1.5 < d ≤2	2 < d ≤ 2.5	2.5 < d ≤ 3	3 ≤d ≤40	40< d ≤63	63 < d ≤100	100 < d ≤ 150	150 < d ≤ 250
S275	S275JR	15	16	17	18	19	23	22	21	19	18
	S275J0 (S275JO)
	S275J2	13	14	15	16	17	21	20	19	19	18