| Hangahanga matū |
| Koeke maitai |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Cu |
| 35CrMo |
0.38～0.45% |
0.17～0.37% |
0.50～0.80% |
≤0.035% |
≤0.035% |
0.90～1.20% |
0.15～0.25% |
≤0.30% |
Nga taonga miihini
| Kaha tuku σs/MPa (>=) |
Te kaha matara σb/MPa (>=) |
Te whakaroa
δ5/% (>=) |
Te whakahekenga o
horahanga ψ/% (>=) |
Pānga pūngao mimiti Aku2/J (>=) |
Te pakeke HBS
100/3000 mōrahi |
| ≥930(95) |
≥1080(110) |
≥12 |
≥45 |
≥78(8) |
≤217HB |
Hei whakanui ake i te oranga o te mate ki te neke atu i te 800,000 nga wa mate, ka taea te whakapakeke i te rino i mua i te whakapakeke ma te tiini me te whakamahana iti. A, no te tinei, whakamahana i te 500-600 ℃ mo te 2-4 haora, ka pupuri i te 850-880 ℃ mo tetahi wa (i te iti rawa 2 haora), ka maka ki te hinu ka whakamatao ki te 50-100 ℃ me hau mātao, ka taea e te pakeke tae 50 i muri tinei -52HRC, i roto i te tikanga ki te aukati i ngatata, 200 ℃ iti pāmahana tempering maimoatanga kia kawea i roto i tonu. I muri i te whakama, ka taea te pupuri i te pakeke i runga ake i te 48HRC.
42CrMo Steel Heat Treatment
Te whakaene
Te whakamahana i roto i te 760±10 ℃, ka whakamatao te oumu ki te 400 ℃ ka whakamahana hau.
Whakaritea
Te whakarite i roto i te 760±10 ℃, ka whakamatao te hau i muri mai i te oumu.
Nga Panui mo te Tiini me te Whakapaipai
Me whakarongo ki te pāmahana o te wai whakamatao. Me whakarite kia kore he paranga hinu me etahi atu poke. Ki te kore, karekau te pakeke o te rino e ranea, ka kore ranei i te pauna.
Te tineia me te whakamahana mo nga taonga rino pire me te kore e tukatuka, katahi ka pakeke kore-rite. Na ko te tukatuka o te maaka, te huri ranei i mua i te Q+T.