Kompożizzjoni kimika tal-azzar AISI 4140
| Grad |
Ċ |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
| 42CrMo |
0.38-0.45 |
0.17-0.37 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.2 |
0.15-0.25 |
- |
| SCM440 |
0.38-0.43 |
0.15-0.35 |
0.6-0.85 |
≤0.035 |
≤0.04 |
0.9-1.2 |
0.15-0.30 |
- |
| 42crmo4/1.7225 |
0.38-0.45 |
≤ 0.4 |
0.6-0.9 |
≤0.025 |
≤0.035 |
0.9-1.2 |
0.15-0.30 |
- |
| 4140 |
0.38-0.43 |
0.15-0.35 |
0.75-1.00 |
≤0.035 |
≤0.04 |
0.8-1.1 |
0.15-0.25 |
- |
| EN19/709M40 |
0.35-0.45 |
0.15-0.35 |
0.5-0.80 |
≤0.035 |
≤0.035 |
0.9-1.5 |
0.2-0.40 |
- |
Proprjetajiet mekkaniċi tal-azzar AISI 4140 (għal gwida biss)
| Grad |
Saħħa tat-tensjoni
σb(MPa) |
Saħħa ta 'rendiment
σs (MPa) |
Titwil
δ5 (%) |
Tnaqqis
ψ (%) |
Valur tal-Impatt
Akv (J) |
Ebusija |
| 4140 |
≥1080 |
≥930 |
≥12 |
≥45 |
≥63 |
28-32HRC |
Ħarsa ġenerali ta' l-azzar AISI 4140
| Daqs |
Round |
Dia 6-1200mm |
| Pjanċa/Flat/Blokk |
Ħxuna
6mm-500mm |
Wisa'
20mm-1000mm |
| Trattament tas-sħana |
Normalizzat; Ittemprat; Imkeffa; Ittemprat |
| Kondizzjoni tal-wiċċ |
Iswed; Imqaxxar; Illustrat; Makkinarju; Mitħun; Imdawwar; Mitħun |
| Kundizzjoni tal-kunsinna |
Falsifikati; Irrumblat bis-sħana; Cold drawn |
| Test |
Saħħa tat-tensjoni, Saħħa ta 'rendiment, elongazzjoni, żona ta' tnaqqis, valur ta 'impatt, ebusija, daqs tal-qamħ, test ultrasoniku, spezzjoni ta' l-Istati Uniti, ittestjar ta 'partiċelli manjetiċi, eċċ. |
| Termini ta 'ħlas |
T/T;L/C;/Money gram/ Paypal |
| Termini tal-kummerċ |
FOB; CIF; C&F; eċċ.. |
| Ħin tal-kunsinna |
30-45 jum |
| Applikazzjoni |
L-azzar AISI 4140 isib ħafna applikazzjonijiet bħala forġa għall-industriji aerospazjali, taż-żejt u tal-gass, tal-karozzi, agrikoli u tad-difiża eċċ.
Applikazzjonijiet tipiċi għall-użi tal-azzar 4140 jinkludu: gerijiet falsifikati, magħżel, attrezzaturi, jigs, għenuq, Fusien, partijiet tal-conveyor, crow bars, partijiet tal-qtugħ, xaftijiet, sprockets, studs, pinions, xaftijiet tal-pompi, imtaten, u gerijiet taċ-ċirku eċċ |
Proprjetajiet Fiżiċi
Il-proprjetajiet fiżiċi tal-azzar liga AISI 4140 huma enfasizzati fit-tabella li ġejja.
| Proprjetajiet |
Metriku |
Imperjali |
| Densità |
7.85 g/ċm3 |
0.284 lb/in³ |
| Punt tat-tidwib |
1416°C |
2580°F |
Proprjetajiet Mekkaniċi
It-tabella li ġejja tiddeskrivi l-proprjetajiet mekkaniċi tal-azzar liga AISI 4140.
| Proprjetajiet |
Metriku |
Imperjali |
| Saħħa tat-tensjoni |
655 MPa |
95000 psi |
| Saħħa ta 'rendiment |
415 MPa |
60200 psi |
| Modulu tal-massa (tipiku għall-azzar) |
140 GPa |
20300 ksi |
| Shear modulus (tipiku għall-azzar) |
80 GPa |
11600 ksi |
| Modulu elastiku |
190-210 GPa |
27557-30458 ksi |
| Proporzjon ta' Poisson |
0.27-0.30 |
0.27-0.30 |
| Titwil fil-waqfa (f'50 mm) |
25.70% |
25.70% |
| Ebusija, Brinell |
197 |
197 |
| Ebusija, Knoop (ikkonvertit minn ebusija Brinell) |
219 |
219 |
| Ebusija, Rockwell B (ikkonvertit minn ebusija Brinell) |
92 |
92 |
| Ebusija, Rockwell C (konvertita minn ebusija Brinell. Valur taħt il-firxa normali HRC, għal skopijiet ta' tqabbil biss) |
13 |
13 |
| Ebusija, Vickers (ikkonvertit minn ebusija Brinell) |
207 |
207 |
| Makkinabilità (ibbażata fuq AISI 1212 bħala 100 makkinabilità) |
65 |
65 |
Proprjetajiet Termali
Il-proprjetajiet termali tal-azzar liga AISI 4140 huma mogħtija fit-tabella li ġejja.
| Proprjetajiet |
Metriku |
Imperjali |
| Koeffiċjent ta' espansjoni termali (@ 0-100°C/32-212°F) |
12.2 µm/m°C |
6.78 µin/in°F |
| Konduttività termali (@ 100°C) |
42.6 W/mK |
296 BTU fi/hr.ft².°F |
Denominazzjonijiet oħra
Denominazzjonijiet oħra ekwivalenti għall-azzar liga AISI 4140 huma elenkati fit-tabella li ġejja.
| AMS 6349 |
ASTM A193 (B7, B7M) |
ASTM A506 (4140) |
ASTM A752 (4140) |
| AMS 6381 |
ASTM A194 (7, 7M) |
ASTM A513 |
ASTM A829 |
| AMS 6382 |
ASTM A29 (4140) |
ASTM A513 (4140) |
SAE J1397 (4140) |
| AMS 6390 |
ASTM A320 (L7, L7M, L7D) |
ASTM A519 (4140) |
SAE J404 (4140) |
| AMS 6395 |
ASTM A322 (4140) |
ASTM A646 (4140) |
SAE J412 (4140) |
| AMS 6529 |
ASTM A331 (4140) |
ASTM A711 |
|
Fabbrikazzjoni u Trattament tas-Sħana
Makkinabilità
L-azzar liga AISI 4140 għandu makkinarju tajjeb fil-kondizzjoni ittemprat.
Li jiffurmaw
L-azzar liga AISI 4140 għandu duttilità għolja. Jista 'jiġi ffurmat bl-użu ta' tekniki konvenzjonali fil-kondizzjoni ittemprat. Jeħtieġ aktar pressjoni jew forza għall-iffurmar minħabba li hija aktar iebsa minn azzar tal-karbonju sempliċi.
Iwweldjar
L-azzar liga AISI 4140 jista 'jiġi wweldjat bl-użu tat-tekniki konvenzjonali kollha. Madankollu, il-proprjetajiet mekkaniċi ta 'dan l-azzar se jiġu affettwati jekk ikun iwweldjat fil-kondizzjoni trattat bis-sħana, u għandu jitwettaq trattament tas-sħana wara l-iwweldjar.
Trattament tas-Sħana
L-azzar liga AISI 4140 jissaħħan f'845 ° C (1550 ° F) segwit minn quenching fiż-żejt. Qabel ma tibbies, tista 'tiġi normalizzata billi tissaħħanha f'913 ° C (1675 ° F) għal perjodu twil ta' żmien, segwit minn tkessiħ bl-arja.
Forġa
L-azzar liga AISI 4140 huwa falsifikat f'926 sa 1205 ° C (1700 sa 2200 ° F)
Ħidma sħuna
L-azzar liga AISI 4140 jista 'jinħadem bis-sħana f'816 sa 1038 ° C (1500 sa 1900 ° F)
Xogħol Biesaħ
L-azzar liga AISI 4140 jista 'jinħadem fil-kesħa bl-użu ta' metodi konvenzjonali fil-kondizzjoni ittemprat.
Ittemprar
L-azzar liga AISI 4140 huwa ittemprat f'872 ° C (1600 ° F) segwit minn tkessiħ bil-mod fil-forn.
Ittemprar
L-azzar liga AISI 4140 jista 'jiġi ttemprat f'205 sa 649 °C (400 sa 1200 °F) skont il-livell ta' ebusija mixtieq. L-ebusija tal-azzar tista 'tiżdied jekk ikollu temperatura aktar baxxa tat-tempra. Pereżempju, saħħa tat-tensjoni ta '225 ksi tista' tinkiseb billi tittempra f'316 °C (600 °F), u saħħa tat-tensjoni ta '130 ksi tista' tinkiseb billi tittempra f'538 °C (1000 °F).
Ebusija
L-azzar liga AISI 4140 jista 'jiġi mwebbes permezz ta' xogħol kiesaħ, jew tisħin u tkessiħ.