EN10155 S235 J0W chitsulo

EN10155 S235 J0W zitsulo mbale, pansi pa EN 10155 muyezo, tikhoza kuona S235J0W zitsulo mbale ngati Steel Resistant to Atmospherical Corrosion.S235J0W mbale yachitsulo ndi imodzi makamaka ya Steel Resistant to Atmospherical Corrosion, S235W0W yokhala ndi zitsulo zotsika, S235J0W yokhala ndi zitsulo zotsika. kutentha madzi a m'nyanja. Chitsulo cha S235J0W ndi chitsulo chopangidwa ndi chitsulo chomwe chimagwiritsidwa ntchito pomanga milatho ndi nyumba.

Mafotokozedwe:
makulidwe: 3mm-150mm
M'lifupi: 30mm-4000mm
Utali: 1000mm--12000mm
Standard: ASTM EN10025 JIS GB

S235J0W  sheet sheet Kusanthula Chemical -% ndi  misa*

Maphunziro	C	Si	Mn	P	S	Ku	Cr	Ndi
	max	max	max	max	max.	max	max	max
S235 J0W	0.13	0.4	0.20-1.66	0.035	0.035	0.25-0.55	0.40-0.80	0.65

S235J0W  sheet sheet Mechanical  katundu

MaphunziroS235 JOW	Yield StrengthReH[N/mm2]transv.min		TensileStrengthRm[N/mm2]transv		FractureElongation[%]transv. min.		Notch ImpactEnergy1)Ch V Complete sampuliutali. mphindi [J]
	e2) ≤ 16	e2)> 16	e2) <3	e2)≥3	e2) ≤2	e2) ≤2
	235	225	360 mpaka 510	360 mpaka 510	19/17	20/18	-

Norman

Europa	Werkst.-Nr.	DE	US	Salzgitter Flachstahl	FK1)
EN 10025-5		SEW0 087	Chithunzi cha ASTM
Chithunzi cha S235J0W	1.8958	-	-	Zithunzi za 360	A
Chithunzi cha S235J2W	1.8961	Chithunzi cha 37-3	-	Zonse za 360 F	A
Chithunzi cha S355J0WP	1.8945	-	-	Allwesta 510 P	B
Chithunzi cha S355J2WP	1.8946	-	Mtundu wa A242	Zithunzi za Allwesta 510 FP	B
Chithunzi cha S355J0W	1.8959	-	ndi 588	Zithunzi za 510	B
Mtengo wa S355J2W	1.8965	Mtengo wa 52-3	-	ALLWESTA 510 F	B
Mtengo wa S355K2W	1.8967	-	-	ALLWESTA 510 F 40	B

FK = Festigkeitsklasse, siehe Abmessungen
Chemische Zusammensetzung in Gewichtsprozent [%] (Schmelzenanalyse)

Sinthani	C	Si	Mn	P	S	N	Cr
	max.	max.			max.	max.
S235J0W1)	0,13	0,40	0,20 - 0,60	max. 0,035	0,035	0,0092) 3)	0,40 - 0,80
S235J2W1)	0,13	0,40	0,20 - 0,60	max. 0,035	0,030	- 4)	0,40 - 0,80
S355J0WP1)	0,12	0,75	max. 1, 0	0,06 - 0,15	0,035	0,0093)	0,30 - 1,25
S355J2WP1)	0,12	0,75	max. 1, 0	0,06 - 0,15	0,030	- 4)	0,30 - 1,25
S355J0W1)5)	0,16	0,50	0,50 - 1,50	max. 0,035	0,035	0,0092) 3)	0,40 - 0,80
S355J2W1)5)	0,16	0,50	0,50 - 1,50	max. 0,030	0,030	- 4)	0,40 - 0,80
S355K2W1)5)	0,16	0,50	0,50 - 1,50	max. 0,030	0,030	- 4)	0,40 - 0,80

Die Stähle enthalten 0,25 bis 0,55% Cu und max. 0,65% Ndi.
Eine Überschreitung des angegebenen Höchstwertes ist zulässig, wenn je 0,001% N ein um 0,005% unter dem festgelegten Höchstwert liegender Phosphorgehalt eingehalten wird. Der Stickstoffgehalt beträgt jedoch höchstens 0,012 % in der Schmelzenanalyse.
Der Höchstwert für den Stickstoffgehalt gilt nicht, wenn die Stähle mindestens 0,020 % Altotal oder genügend Gehalte an anderen stickstoffabbindenden Elementen aufweisen.
Die Stähle enthalten mindestens eines der folgenden Elemente: Zonse: ≥ 0,020 %, Nb: 0,015 - 0,060%, V: 0,02 - 0,12%, Ti: 0,02 - 0,10 %. Wenn die Elemente in Kombination angewendet werden, ist mindestens eines von ihnen mit dem angegebenen Mindestgehalt enthalten.
Die Stähle dürfen max. 0,30% Mo ndi max. 0,15% Zr enthalten.
Mechanische Eigenschaften1)

Sinthani	Probenlage	Min. Streckgrenze2) [MPa]		Zugfestigkeit2) [MPa]		Min. Bruchdehnung2) [%]
						L0 = 80 mm			L0 = 5,65 √S0
		ndi ≤16	ndi> 16	ndi <3	ndi ≥3	e≤2	2 ndi <2,5	2,5 ndi <3	ndi ≥3
Chithunzi cha S235J0W	l/t	235	225	360 - 510	360 - 510	19/17	20/18	21/19	26/24
Chithunzi cha S235J2W	l/t	235	225	360 - 510	360 - 510	19/17	20/18	21/19	26/24
Chithunzi cha S355J0WP	l/t	3553)	-	510 - 680	4703) - 6303)	16/14	17/15	18/16	22/203)
Chithunzi cha S355J2WP	l/t	3553)	-	510 - 680	4703) - 6303)	16/14	17/15	18/16	22/203)
Chithunzi cha S355J0W	l/t	355	345	510 - 680	470 - 630	16/14	17/15	18/16	22/20
Mtengo wa S355J2W	l/t	355	345	510 - 680	470 - 630	16/14	17/15	18/16	22/20
Mtengo wa S355K2W	l/t	355	345	510 - 680	470 - 630	16/14	17/15	18/16	22/20

Die in der Tabelle angegebenen Werte des Zugversuches gelten für Längsproben (I) außer bei Band und Blech ≥ 600 mm Breite, aus denen Querproben (t) zu entnehmen sind.
e = Nenndick mu mm
S355J0WP ndi S355J2WP: e 12 ≤ mm
Kerbschlagarbeit im Lieferzustand (Mindestwerte an Charpy-V-Proben)

Sinthani	Kutentha [°C]	Kerbschlagarbeit1) [J]
Chithunzi cha S235J0W	0	27
Chithunzi cha S235J2W	-20	27
Chithunzi cha S355J0WP	0	27
Chithunzi cha S355J2WP	-20	27
Chithunzi cha S355J0W	0	27
Mtengo wa S355J2W	-20	27
Mtengo wa S355K2W	-20	40

Mittelwerte kapena 3 Proben; ein Einzelwert darf den geforderten Mindeswert umhöchstens 30 % unterschreiten. Für Erzeugnisdicken von 6 - 10 mm entspricht die Probenbreite der jeweiligen Erzeugnisdicke, wobei die Prüfung an Charpy-V-ähnlichen Proben erfolgt. Die in der oberen Tabelle angegebenen Werte verringern sich hierbei proportional zur Probenbreite.
Prinzip der Deckschichtbildung

s355jow zitsulo mbale Properties
Chemical Properties Of s355jow Steel Plate

Gulu	C	Si	Mn	P	S	N	Kuwonjezera kwa mgwirizano wa nayitrogeni zinthu	Cr	Ku
Chithunzi cha S355J0W	0.16	0.50	0.50/1.50	0.035	0.035	0.009	-	0.40/0.80	0.25/0.55

Mechanical Properties Of s355jow Steel Plate

Gulu	Min. Zokolola Mphamvu Reh MPa						Mphamvu Yamphamvu Rm MPa
	Kunenepa mwadzina (mm)						Kunenepa mwadzina (mm)
	≤16	> 16 ≤40	>40 ≤63	> 63 ≤80	> 80 ≤100	>100 ≤150	>3	>3 ≤100	>100 ≤150
Chithunzi cha S355J0W	355	345	335	325	315	295	510/680	470/630	450/600

MAFUNSO OFANANA

Zofunika #	Mtengo wa EN 10155	SEW0 087	NFA 35-502	UNI	Chithunzi cha BS4360	Chithunzi cha ASTM	Chithunzi cha JIS G3114
1.8961	Chithunzi cha S235J2W	Chithunzi cha 37-3	E24W4	Mtengo wa 360DK1	-	-	-
1.8945	Chithunzi cha S355J0WP	E36 WA 3	Mtengo wa 510C1K1	Mtengo wa WR50A	-	-	-
1.8946	Chithunzi cha S355J2WP	-	E36 WA 4	Mtengo wa 510D1K1	-	Mtundu wa A242	-
1.8959	Chithunzi cha S355J0W	-	E36 WB3	Mtengo wa 510C2K1	Mtengo wa 50B	A 588 - A 242 Gr. 1	Chithunzi cha SMA50AW
1.8963	Chithunzi cha S355J2G1W	Mtengo wa 52-3	-	Chithunzi cha 510D2K1	Mtengo wa WR50C	ndi 588g. A	ku
1.8965	Chithunzi cha S355J2G2W	-	-	-	-	-	Zithunzi za SMA50CP
1.8966	Chithunzi cha S355K2G1W	-	E36 WB4	-	-	ndi 709g. 50 W	-
1.8967	Zithunzi za S355K2G2W	-	-	-	-	-	-