Kelas baja E24W4 mangrupikeun produk anu digulung panas tina baja struktural dina kaayaan pangiriman téknis kalayan résistansi korosi atmosfir anu ningkat.
Baja E24W4 mangrupikeun sasmita anu sami sareng baja S235J2W (1.8961) dina standar EN 10025 - 5: 2004 sareng baja WTSt 37-3 dina standar SEW087 sareng baja Fe360DK1 dina standar UNI.
spésifikasi:
Ketebalan: 3mm--150mm
rubak: 30mm--4000mm
Panjangna: 1000mm--12000mm
Standar: ASTM EN10025 JIS GB
E24W4 Steel Komposisi Kimia
| C% | Mn% | Cr% | Si % | CEV% | S % |
| Max 0.13 | 0.2-0.6 | 0.4-0.8 | Max 0.4 | Max 0,44 | Max 0.3 |
| Cu% | P% | ||||
| 0.25-0.55 | Max 0,035 |
E24W4 Steel Sipat mékanis
| Kelas | Min. Kakuatan ngahasilkeun Mpa | Kakuatan Tensile MPa | Dampak | ||||||||
| E24W4 | Ketebalan Nominal (mm) | Ketebalan Nominal (mm) | gelar | J | |||||||
| Kandel mm | ≤16 | > 16 ≤40 |
>40 ≤63 |
> 63 ≤80 |
>80 ≤100 |
> 100 ≤150 |
≤3 | > 3 ≤100 | > 100 ≤150 | -20 | 27 |
| E24W4 | 235 | 225 | 215 | 215 | 215 | 195 | 360-510 | 360-510 | 350-500 | ||
Nilai uji tensile anu dirumuskeun dina tabél manglaku ka sampel longitudinal; dina hal strip jeung lambar baja tina rubak ≥600 mm aranjeunna dilarapkeun ka sampel transverse.
Lamun sipat mékanis E24W4 geus nyata dirobah ku coldforming beurat, boh stress relief annealing atawa dinormalisasi bisa dilarapkeun. Dinormalisasi ogé kedah diterapkeun saatos pembentukan panas di luar kisaran suhu 750 - 1.050 °C sareng saatos panas teuing.