34CrNiMo6 Himiki düzümi we ekwiwalent polat derejeli häsiýetleri
| BS EN 10083 - 3: 2006 |
34CrNiMo6 |
C. |
Si |
Si |
S. |
S. |
Cr |
Mo. |
Ni |
| 0.30-0.38 |
0.40 Maks |
0.50-0.80 |
Iň ýokary 0.025 |
Iň ýokary 0.035 |
1.30-1.70 |
0.15-0.30 |
1.30-1.70 |
34CrNiMo6 Polat mehaniki aýratynlyklary
| Diametri (mm) |
<16 |
16~ 40 |
40~100 |
100~160 |
160 ~250 |
| Galyňlygy t (mm) |
<8 |
8~20 |
20~60 |
60~100 |
100~160 |
| Dartyş güýji Rm (N / mm2) |
1200 - 1400 |
1100 - 1300 |
1000 - 1200 |
900 - 1100 |
800 - 950 |
| Uzalma A (%) |
9 min |
10 min |
11 min |
Min 12 |
13 min |
| Z meýdanynyň azalmagy (%) |
40Min |
45 min |
50Min |
55Min |
55Min |
| Çydamlylyk CVN (J) |
35Min |
45 minut |
45 minut |
45 minut |
45 min |
| Hasyl güýji Re (N / mm²) |
1000 min |
900 min |
800 min |
700 min |
600 min |
EN 34CrNiMo6 Polat standartlary we şoňa meňzeşler
| BS EN 10083 -3: 2006 |
34CrNiMo6 / 1.6582 |
ASTM A29: 2004 |
4337 |
| BS EN 10250 - 3: 2000 |
3. EN / DIN 34CrNiMo6 Polat himiki düzüminiň aýratynlyklary
| BS EN 10083 - 3: 2006 |
34CrNiMo6
/1.6582 |
C. |
Mn |
Si |
S. |
S. |
Cr |
Mo. |
Ni |
| 0.30-0.38 |
0.5-0.8 |
Iň ýokary 0,40 |
Iň ýokary 0.025 |
Iň ýokary 0.035 |
1.3-1.7 |
0.15-0.30 |
1.3-1.7 |
| BS EN 10250-3: 2000 |
C. |
Mn |
Si |
S. |
S. |
Cr |
Mo. |
Ni |
| 0.30-0.38 |
0.5-0.8 |
Iň ýokary 0,40 |
Iň ýokary 0.035 |
Iň ýokary 0.035 |
1.3-1.7 |
0.15-0.30 |
1.3-1.7 |
| ASTM A29: 2004 |
4337 |
C. |
Mn |
Si |
S. |
S. |
Cr |
Mo. |
Ni |
| 0.30-0.40 |
0.6-0.8 |
0.20-0.35 |
Iň ýokary 0.035 |
Iň ýokary 0.040 |
0.70-0.90 |
0.20-0.30 |
1.65-2.00 |
4. EN / DIN 34CrNiM06 / 1.6582 garyndy polatyň mehaniki aýratynlyklary
| Sypatlar |
<16 |
> 16-40 |
> 40 - 100 |
> 100 - 160 |
> 160 - 250 |
| Galyňlygy t [mm] |
<8 |
8
20
60
| 100
| | | |
| Hasyl güýji Re [N / mm²] |
min. 1000 |
min. 900 |
min. 800 |
min. 700 |
min. 600 |
| Dartyş güýji Rm [N / mm2] |
1200 - 1400 |
1100 - 1300 |
1000 - 1200 |
900 - 1100 |
800 - 950 |
| Uzalma A [%] |
min. 9 |
min. 10 |
min. 11 |
min. 12 |
min. 13 |
| Z meýdanynyň azalmagy [%] |
min. 40 |
min. 45 |
min. 50 |
min. 55 |
min. 55 |
| Çydamlylyk CVN [J] |
min. 35 |
min. 45 |
min. 45 |
min. 45 |
min. 45 |
5. 34CrNiMo6 in Engineeringenerçilik polatynyň gyzgyn bejergisi
34CrNiMo6 polatdan söndürilen we temperatura (Q + T)
- 34CrNiMo6 tegelek polady 850 ° C temperaturada ýuwaş-ýuwaşdan gyzdyryň;
- Bu gatylaşýan temperatura söndürilende ýagda batyryň;
- 34CrNiMo6 polat otag temperaturasyna ýeten badyna temperatura.
- Degişli temperaturada birmeňzeş gyzdyryň;
- Ojakdan çykaryň we howada salkynlaň.
- Adaty temperatura temperaturasy, hakyky talaplara baglylykda 600 ° C.
6. DIN 34CrNiMo6 / 1.6582 polat
Gyzgyn emele gelýän temperatura: 1100-900oC.
7. Polat 34CrNiMo6
Işlemek iň oňat 1.6582 garyndy polat bilen örtülen ýa-da kadalaşdyrylan we gyzgyn ýagdaýda ýerine ýetirilýär. Conventionhli adaty usullar bilen işlenip bilner.
8. Kebşirlemek
Garyndy materiallary birleşdirilip ýa-da kebşirlenip bilner. Bu garyndyny bellenilen usullar bilen kebşirlände ýylylyk bilen kebşirlemek proseduralary berjaý edilmelidir.
9. Arza
EN DIN 34CrNiMo6 polat gowy plastisit we ýokary güýç talap edýän gurallary ýasamak üçin ulanylýar. Adatça agyr tehnika oky, turbinaly pyçak, köp sanly geçiriji bölekler, berkidijiler, krank şkaflary, dişli enjamlar, şeýle hem motor gurluşygy üçin agyr ýüklenen bölekler ýaly uly ululyklary we möhüm bölekleri ýasamak üçin saýlanýar.
Gnee Steel in engineeringenerçilik 34CrNiMo6 polat / 1.6582 in engineeringenerçilik garyndy polatlary bilen üpjün etmek üçin ygtybarly. Jikme-jik talaplaryňyzy bize aýdyň we ýakyn wagtda iň gowy teklip hödürläň.