ASTM A588 / A588M bakal

Standard na detalye para sa high-strength low-alloy structural steel, hanggang 50 ksi [345 MPa] minimum yield point, na may atmospheric corrosion resistance.
Ang kinakailangang ASTM G101 Corrosion Resistance Index ay dapat na ≥ 6.0. Bilang karagdagan sa karaniwang aplikasyon sa mga welded na tulay at gusali, ang detalye ay karaniwang ginagamit din sa mga pampasaherong sasakyang tren.

Ang mga pagtutukoy:
Kapal: 3mm--150mm
Lapad: 30mm--4000mm
Haba: 1000mm--12000mm
Pamantayan: ASTM EN10025 JIS GB

ASTM A588 Komposisyon ng Kemikal

A588 Komposisyon ng Bakal
	Grade A	Baitang B	Grade K		Baitang C
Carbon	0.19%	0.2%	0.17%		0.17%
Manganese	0.8-1.25%	0.75-1.35%	0.50-1.20%		0.50-1.20%
Posporus	0.03%	0.03%	0.03%		0.03%
Sulfur	0.03%	0.03%	0.03%		0.03%
Silicon	0.30-0.65%	0.15-0.50%	0.25-0.50%		0.25-0.50%
Nikel	0.4%	0.5%	0.4%		0.4%
Chromium	0.4-0.65%	0.4-0.7%	0.4-0.7%		0.4-0.7%
Molibdenum	...	...	0.1%		0.1%
tanso	0.25-0.4%	0.2-0.4%	0.3-0.5%		0.3-0.5%
Vanadium	0.02-0.10%	0.01-0.10%	...
Columbia	...	...	0.005-0.05%		0.005-0.05%

Mga Katangian ng Plate

Mga Katangian ng Grade A588

BAITANG	KAPAL	MAKUAT KSI	YIELD KSI	% MATAGAL. MIN
				8"	2"
A588	.75"THRU 4"	70MIN	50 YP MIN	16	19
	>4"THRU 4"	67MIN	46 YP MIN	-
	>5"THRU 8"	63MIN	42 YP MIN

Ari-arian
Tensile: 70 ksi min (4 pulgada pababa), 67 ksi min (4-5) 63 ksi min (Higit sa 5-8)
Yield: 50 ksi min (4 pababa), 46 ksi min (4- 5) 42 ksi min (Higit sa 5-8)
Pagpahaba: 16 porsiyentong min sa 8 pulgada 19 porsiyentong min sa 2 pulgada (para sa mga plato na mas malawak sa 24 pulgada) sa sheet.
Mga Karaniwang Gamit
Ang bakal na ito ay maaaring iwanang hindi pininturahan na ginagawa itong mainam na aplikasyon kabilang ang mga tulay, gusali, at iba pang istruktura.