S235J0W çelik sac Kimyasal analiz - kütle %'si*
| notlar |
C |
Si |
Mn |
P |
S |
cu |
cr |
Ni |
| maks. |
maks. |
maks. |
maks. |
maks. |
maks. |
maks. |
maks. |
| S235 J0W |
0.13 |
0.4 |
0.20-1.66 |
0.035 |
0.035 |
0.25-0.55 |
0.40-0.80 |
0.65 |
S235J0W çelik sac Mekanik özellikler
| SınıflarS235 JOW |
Akma DayanımıReH[N/mm2]transv.min |
Gerilme DayanımıRm[N/mm2]transv |
Kırılma Uzama[%]transv. dk. |
Notch ImpactEnergy1)Ch Vtam örnek boylam. dk [J] |
| e2) ≤ 16 |
e2)> 16 |
e2)< 3 |
e2)≥3 |
e2) ≤ 2 |
e2) ≤ 2 |
|
| 235 |
225 |
360 ila 510 |
360 ila 510 |
19/17 |
20/18 |
- |
Normen
| Avrupa |
Werkst.-Nr. |
Almanya |
BİZ |
Salzgitter Flachstahl |
FK1) |
| EN 10025-5 |
|
DİKİŞ 087 |
ASTM |
|
|
| S235J0W |
1.8958 |
- |
- |
Allwesta 360 |
A |
| S235J2W |
1.8961 |
WTSt 37-3 |
- |
Allwesta 360 F |
A |
| S355J0WP |
1.8945 |
- |
- |
Allwesta 510 P |
B |
| S355J2WP |
1.8946 |
- |
A 242 Tip 1 |
Allwesta 510 FP |
B |
| S355J0W |
1.8959 |
- |
bir 588 |
Allwesta 510 |
B |
| S355J2W |
1.8965 |
WTSt 52-3 |
- |
Allwesta 510 F |
B |
| S355K2W |
1.8967 |
- |
- |
Allwesta 510 F 40 |
B |
FK = Festigkeitsklasse, siehe Abmessungen
Gewichtsprozent'te Chemische Zusammensetzung [%] (Schmelzenanalyse)
| sıralama |
C |
Si |
Mn |
P |
S |
N |
cr |
|
maks. |
maks. |
|
|
maks. |
maks. |
|
| S235J0W1) |
0,13 |
0,40 |
0,20 - 0,60 |
maks. 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| S235J2W1) |
0,13 |
0,40 |
0,20 - 0,60 |
maks. 0,035 |
0,030 |
– 4) |
0,40 - 0,80 |
| S355J0WP1) |
0,12 |
0,75 |
maks. 1,0 |
0,06 - 0,15 |
0,035 |
0,0093) |
0,30 - 1,25 |
| S355J2WP1) |
0,12 |
0,75 |
maks. 1,0 |
0,06 - 0,15 |
0,030 |
– 4) |
0,30 - 1,25 |
| S355J0W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
maks. 0,035 |
0,035 |
0,0092) 3) |
0,40 - 0,80 |
| S355J2W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
maks. 0,030 |
0,030 |
– 4) |
0,40 - 0,80 |
| S355K2W1)5) |
0,16 |
0,50 |
0,50 - 1,50 |
maks. 0,030 |
0,030 |
– 4) |
0,40 - 0,80 |
Stähle, %0,25 ila %0,55 Cu ve maks. %0,65 Ni.
Höchstwert Eine Überschreitung des angegebenen Höchstwertes ist zulässig, wenn je 0,001% N ein um 0,005 % of festgelegten Höchstwert liegender Phosphorgehalt eingehalten wird. Der Stickstoffgehalt beträgt jedoch höchstens 0,012 % in the Schmelzenanalyse.
Höchstwert für den Stickstoffgehalt yaldızlı nicht, wenn die Stähle mindestens %0,020 Altotal veya genügend Gehalte ve anderen stickstoffabbindenden Elementen aufweisen.
Stähle enthalten enthaltens eines der folgenden Elemente: Toplam: ≥ 0,020 %, Nb: %0,015 - 0,060, V: %0,02 - 0,12, Ti: %0,02 - 0,10. Kombinasyondaki Unsurları bir araya getirirken, en çok dikkat edilmesi gereken unsurlardan biri olarak kabul edilir.
Die Stähle dürfen max. %0,30 Mo und maks. % 0,15 Zr entalten.
Mekanizma Eigenschaften1)
| sıralama |
araştırma |
dak. Streckgrenze2) [MPa] |
Zugfestigkeit2) [MPa] |
dak. Bruchdehnung2) [%] |
|
|
|
|
|
|
L0 = 80 mm |
L0 = 5,65 √S0 |
|
|
e ≤ 16 |
e > 16 |
e<3 |
e ≥ 3 |
e≤2 |
2< e < 2,5 |
2,5 < e < 3 |
e ≥ 3 |
| S235J0W |
l/t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| S235J2W |
l/t |
235 |
225 |
360 - 510 |
360 - 510 |
19/17 |
20/18 |
21/19 |
26/24 |
| S355J0WP |
l/t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| S355J2WP |
l/t |
3553) |
- |
510 - 680 |
4703) - 6303) |
16/14 |
17/15 |
18/16 |
22/203) |
| S355J0W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| S355J2W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
| S355K2W |
l/t |
355 |
345 |
510 - 680 |
470 - 630 |
16/14 |
17/15 |
18/16 |
22/20 |
Die in der Tabelle angegebenen Werte des Zugversuches gelten für Längsproben (I) to bei Band and Blech ≥ 600 mm Breite, aus denenen Querproben (t) zu entnehmen sind.
e = mm cinsinden Nenndicke
S355J0WP ve S355J2WP: e 12 ≤ mm
Kerbschlagarbeit im Lieferzustand (Mindestwerte ve Charpy-V-Proben)
| sıralama |
Sıcaklık [°C] |
Kerbschlagarbeit1) [J] |
|
|
|
| S235J0W |
0 |
27 |
| S235J2W |
-20 |
27 |
| S355J0WP |
0 |
27 |
| S355J2WP |
-20 |
27 |
| S355J0W |
0 |
27 |
| S355J2W |
-20 |
27 |
| S355K2W |
-20 |
40 |
Mittelwerte aus 3 Proben; Bir Einzelwert darf den geforderten Mindestwert um höchstens 30 % unterschreiten. Für Erzeugnisdicken von 6 - 10 mm entspricht die Probenbreite der jeweiligen Erzeugnisdicke, wobei die Prüfung and Charpy-V-ähnlichen Proben erfolgt. Ölçmek, orantılı olarak mümkün olan en yüksek orantıda olabilir.
Prinzip der Deckchichtbildung
s355jow çelik levha Özellikleri
s355jow Çelik Levhanın Kimyasal Özellikleri
| Seviye |
C |
Si |
Mn |
P |
S |
N |
eklenmesi
nitrojen bağlama
elementler |
cr |
cu |
| S355J0W |
0.16 |
0.50 |
0.50/1.50 |
0.035 |
0.035 |
0.009 |
– |
0.40/0.80 |
0.25/0.55 |
s355jow Çelik Levhanın Mekanik Özellikleri
| Seviye |
dak. Akma Dayanımı Reh MPa |
Çekme Dayanımı Rm MPa |
| Nominal Kalınlık (mm) |
Nominal Kalınlık (mm) |
| ≤16 |
>16 ≤40 |
>40 ≤63 |
>63 ≤80 |
>80 ≤100 |
>100 ≤150 |
>3 |
>3 ≤100 |
>100 ≤150 |
| S355J0W |
355 |
345 |
335 |
325 |
315 |
295 |
510/680 |
470/630 |
450/600 |
EŞDEĞER ÖZELLİKLER
| Malzeme # |
EN 10155 |
DİKİŞ 087 |
NFA 35-502 |
UNI |
BS 4360 |
ASTM |
|
| 1.8961 |
S235J2W |
WTSt 37-3 |
E 24 K 4 |
Fe 360K 1 |
– |
– |
– |
| 1.8945 |
S355J0WP |
E 36 WA 3 |
Fe 510 C1K1 |
WR 50 bir |
– |
– |
– |
| 1.8946 |
S355J2WP |
– |
E 36 WA 4 |
Fe 510 D1K1 |
– |
A 242 Tip 1 |
– |
| 1.8959 |
S355J0W |
– |
E 36 WB 3 |
Fe 510 C2K1 |
WR 50 B |
A 588 – A 242 Gr. 1 |
SMA 50 AW |
| 1.8963 |
S355J2G1W |
WTSt 52-3 |
– |
Fe 510 D2K1 |
WR 50C |
588 Gr. A |
ile |
| 1.8965 |
S355J2G2W |
– |
– |
– |
– |
– |
SMA 50 CP |
| 1.8966 |
S355K2G1W |
– |
E 36 WB 4 |
– |
– |
709 Gr. 50 W |
– |
| 1.8967 |
S355K2G2W |
– |
– |
– |
– |
– |
– |