A709 100-darajali po'lat plitalar

A709Gr100, A709Gr.100, A709 100 nav, A709 Gr 100, A709Gr100, A709 100 daraja po'lat

Standartni qabul qiling: ASTM A709/A709M-07
Gnee po'lat navi: A709 Gr.36, A709 Gr.50, A709 Gr.50W, A709 Gr.HPS50W/HPS70W, A709 Gr.100/100W, A709 36-sinf, A709-darajali 59A09A, A709-sinf 50 Vt, A709 darajasi HPS50W, A709 darajasi HPS70W, A709 darajasi 100, A709 darajasi 100 Vt, A709 darajasi HPS100W.

A709 100-darajali po'lat plitalar
A709 Grade 100 po'lat navi ko'prik loyihalarida ishlatiladigan yuqori quvvatli past qotishma strukturaviy uglerodli po'latdir.
Xitoyning materik ko'prigi loyihalarida A709 Gr.100 ko'p yillar davomida gnee po'lat yetkazib beradi. Shuningdek, mijozlarimizga shoshilinch ehtiyoj uchun A709 Gr.100 da ko'plab zaxira o'lchamlari mavjud. Endi biz A709 Gr.100 po'lat plitalaridagi xorijdagi po'lat bozorimizni kengaytirmoqdamiz.

A709 100-sinf Kimyoviy tarkibi Issiqlik tahlili

Eslatma 1: ". . .”demak, hech qanday talab yo‘q     A709-sinf 100[690]，100Vt[690W] darajasi Eslatma 2, A,B,C,E,F,H,J,M,P,Q, A 514/A 514M A,B,C,E,F,H,J,M,P,Q po'lat darajasi bir xil
Maks Qalin [mm] da	A turi,％	B turi,％	C turi,％	EA ,％ yozing	FA ,％ yozing	H turi,％	J turi,％	M turi,％	PA ,％ yozing	QA ,％ yozing
	1.25[32]	1.25[32]	11⁄4[32]	4[100]	2.5[65]	2[50]	1.25[32]	2[50]	4[100]	4[100]
C	0,15–0,21	0,12–0,21	0,10–0,20	0,12–0,20	0,10–0,20	0,12–0,21	0,12–0,21	0,12–0,21	0,12–0,21	0,14–0,21
Mn	0,80–1,10	0,70–1,00	1,10–1,50	0,40–0,70	0,60–1,00	0,95–1,30	0,45–0,70	0,45–0,70	0,45–0,70	0,95–1,30
P，maks	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035
S, maks	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035	0.035
Si	0,40–0,80	0,20–0,35	0,15–0,30	0,20–0,40	0,15–0,35	0,20–0,35	0,20–0,35	0,20–0,35	0,20–0,35	0,15–0,35
Ni	...	...	...	...	0,70–1,00	0,30–0,70	...	1,20–1,50	1,20–1,50	1,20–1,50
Cr	0,50–0,80	0,40–0,65	...	1.40–2.00	0,40–0,65	0,40–0,65	...	...	0,85–1,20	1.00–1.50
Mo	0,18–0,28	0,15–0,25	0,15–0,30	0,40–0,60	0,40–0,60	0,20–0,30	0,50–0,65	0,45–0,60	0,45–0,60	0,40–0,60
V	...	0,03–0,08	...	B	0,03–0,08	0,03–0,08	...	...	...	0,03–0,08
Ti	...	0,01–0,03	...	0,01–0,10	...	...	...	...	...	. ..
Zr	0,05–0,15C	...	...	...	...	...	...	...	...	...
Cu	...	...	...	...	0,15–0,50	...	...	...	...	...
B	0,0025–maks	0,0005–0,005	0,001–0,005	0,001–0,005	0,0005–0,006	0,0005–0,005	0,001–0,005	0,001–0,005	0,001–0,005	...

709 gr. 100 mexanik xususiyat

A709 darajasi	Qalin mm	Yo'l bering [MPa]	Kuchlanish [MPa]	Cho'zilish min %				kamaytirish Min %	HB
				Chelik plastinka		Strukturaviy po'lat
				8 dyuym [200 mm]	2 dyuym [50 mm]	8 dyuym [200 mm]	2 dyuym [50 mm]
36[250]	≤100	[250]daq	400-550	20	23	20	21	…	…
		[250]daq	400 min	…	…	20	19	…	…
50[345]	≤100	345 min	450 min	18	21	18	21F	…	…
50S[345S]	G	345-450HI	450 min H	…	…	18	21	…	…
50 Vt [345 Vt] HPS50W[HPS345W]	≤100	345 min	485 min	18	21	18	21J	…	…
HPS70W[HPS485W]	≤100	485 min	585-760	…	19K	…	…	…	…
100 [690], 100 Vt [690 Vt], HPS100 W [HPS690 W]	≤65	690 daqiqa B	760-895	…	18K	…	…	L	235-293 mln
100 [690], 100 Vt [690 Vt],	65-100	620 daqiqa B	690-895	…	16K	…	…	L	…