ASTM A588 / A588M po'latdir

Atmosfera korroziyaga chidamliligi bilan 50 ksi [345 MPa] gacha bo'lgan eng kam rentabellikga ega, yuqori quvvatli past qotishma konstruktiv po'lat uchun standart spetsifikatsiya.
Kerakli ASTM G101 korroziyaga chidamlilik indeksi ≥ 6,0 bo'lishi kerak. Payvandlangan ko'priklar va binolarda odatiy dasturga qo'shimcha ravishda, spetsifikatsiya odatda yo'lovchi temir yo'l vagonlarida ham qo'llaniladi.

Texnik xususiyatlari:
Qalinligi: 3 mm - 150 mm
Kengligi: 30-4000 mm
Uzunligi: 1000-12000 mm
Standart: ASTM EN10025 JIS GB

ASTM A588 Kimyoviy tarkibi

A588 Chelik tarkibi
	A sinf	B sinf	K sinf		C darajasi
Uglerod	0.19%	0.2%	0.17%		0.17%
Marganets	0.8-1.25%	0.75-1.35%	0.50-1.20%		0.50-1.20%
Fosfor	0.03%	0.03%	0.03%		0.03%
Oltingugurt	0.03%	0.03%	0.03%		0.03%
Kremniy	0.30-0.65%	0.15-0.50%	0.25-0.50%		0.25-0.50%
Nikel	0.4%	0.5%	0.4%		0.4%
Chromium	0.4-0.65%	0.4-0.7%	0.4-0.7%		0.4-0.7%
Molibden	...	...	0.1%		0.1%
Mis	0.25-0.4%	0.2-0.4%	0.3-0.5%		0.3-0.5%
Vanadiy	0.02-0.10%	0.01-0.10%	...
Kolumbiya	...	...	0.005-0.05%		0.005-0.05%

Plitalar xususiyatlari

A588 darajasidagi xususiyatlar

BAJA	QALINLIK	TURISH KSI	YIELD KSI	% UZAY. MIN
				8"	2"
A588	.75"TO 4"	70 MIN	50 YP MIN	16	19
	>4"TO 4"	67 MIN	46 YP MIN	-
	>5"THRU 8"	63 MIN	42 YP MIN

Xususiyatlari
Tortishish: 70 ksi min (4 dyuym va undan past), 67 ksi min (4-5) 63 ksi min (5-8 dan ortiq)
Daromad: 50 ksi min (4 va undan kam), 46 ksi min (4-5) 42 ksi min (5-8 dan ortiq)
Cho'zilish: 8 dyuymda 16% min va 2 dyuymda 19% min (24 dyuymdan kengroq plitalar uchun) varaqda.
Oddiy foydalanish
Ushbu po'latni bo'yalmagan holda qoldirish mumkin, bu uni ko'priklar, binolar va boshqa tuzilmalar uchun ideal qo'llash imkonini beradi.