316 / 316L ALAGBARA IRIN

Alloy 316 / 316L jẹ molybdenum-ara austenitic alagbara, irin. Awọn akoonu nickel ati molybdenum ti o ga julọ ni ipele yii ngbanilaaye lati ṣafihan awọn ohun-ini sooro ipata gbogbogbo ti o dara julọ ju 304, Alloy 316 / 316L irin alagbara, irin ni lilo pupọ ni awọn ohun elo iṣowo ati ile-iṣẹ. O ti wa ni ohun austenitic alloy pẹlu ti o dara weldability ati ki o tayọ malleability.

Iyatọ Laarin 316 ati 316L

316 irin alagbara, irin ni o ni diẹ erogba ninu rẹ ju 316L. Eyi rọrun lati ranti, bi L ṣe duro fun "kekere." Ṣugbọn botilẹjẹpe o ni erogba kere, 316L jẹ iru pupọ si 316 ni gbogbo ọna. Iye owo jẹ iru kanna, ati pe awọn mejeeji jẹ ti o tọ, sooro ipata, ati yiyan ti o dara fun awọn ipo wahala-giga.

316L, sibẹsibẹ, jẹ aṣayan ti o dara julọ fun iṣẹ akanṣe kan ti o nilo ọpọlọpọ alurinmorin nitori 316 jẹ ifaragba si ibajẹ weld ju 316L (ibajẹ laarin weld). Sibẹsibẹ, 316 ni a le parẹ lati koju ibajẹ weld. 316L tun jẹ irin alagbara nla fun iwọn otutu giga, ipata giga, eyiti o jẹ idi ti o ṣe gbajumọ fun lilo ninu ikole ati awọn iṣẹ akanṣe okun.

Bẹni 316 tabi 316L jẹ aṣayan ti o din owo julọ. 304 ati 304L jẹ iru ṣugbọn idiyele kekere. Ati pe bẹni ko tọ bi 317 ati 317L, eyiti o ni akoonu molybdenum ti o ga julọ ati pe o dara julọ fun resistance ipata gbogbogbo.

Awọn alaye ọja

Oruko	tutu ti yiyi 304 316 alagbara, irin sheets awo / Circle
Sisanra	0.3-3mm
Standard Iwon	1000 * 2000mm, 1219*2438mm, 1250*2500mm tabi bi onibara ká ibeere
Dada	2B,BA,NO.4,8K,irun irun,etched,pvd awọ ti a bo,egboogi ika ọwọ
Techquine	tutu ti yiyi
Mill igbeyewo ijẹrisi	le ti wa ni nṣe
Iṣura tabi rara	to akojopo
Apeere	wa
Awọn ofin sisan	30% TT bi idogo, iwọntunwọnsi ṣaaju gbigbe
Iṣakojọpọ	stanfard okeere package
Akoko Ifijiṣẹ	laarin 7-10 ọjọ

Kemikali tiwqn

Iru	%C	%Si	%Mn	%P	%S	%Cr	%Ni	%Mo
316	ti o pọju 0.080	1.00 ti o pọju	2.00 ti o pọju	ti o pọju 0.045	ti o pọju 0.030	16.00-18.00	10.00-14.00	2.00-3.00
316L	ti o pọju 0.030	1.00 ti o pọju	2.00 ti o pọju	ti o pọju 0.045	ti o pọju 0.030	16.00-18.00	10.10-14.00	2.00-3.00

International awọn ajohunše

ITA	USA	GER	FRA	UK	RUS	CHN	JAP
X5CrNiMo1712-2	316	1.4401	Z6CND17.11	316S16	08KH16N11M3	0Cr17Ni12Mo2	SUS316
X2CrNiMo1712-2	316L	1.4404	Z3CND17-11-02	316S11	03KH17N14M2	0Cr19Ni12Mo2	SUS316L

Ti ara / darí / gbona / ina / oofa-ini

Ohun ini	Aami	U.o.M.	Iru	Awọn akọsilẹ	Awọn iye
iwuwo	δ	[g/cm3]	Ti ara	Iwọn otutu yara.	7.95
modulus ọdọ	E	[GPa]	Ẹ̀rọ	-	200
Ooru pato	c	[J/kg-K]	Gbona	Iwọn otutu yara.	500
Olusọdipúpọ ti laini igbona imugboroosi	α	[10^-6 /ºC]	Gbona	(ΔT=0-100°C)	17
Gbona elekitiriki	λ	[W/ (m·K)]	Gbona	Iwọn otutu yara.	15.0
Ina resistivity	ρ	[Ω*m*10^-9]	Itanna	-	730
Ojulumo se permeability	µ	-	Oofa	Paramagnetic	1.020*

Imọ data

Ohun ini	Iru	U.o.M.	Awọn iye	U.o.M.	Awọn iye
Lile	Ẹ̀rọ	[HRC]	20 - 39 (1)*	[HV]	100 - 250 (2)*
Gbẹhin agbara fifẹ	Ẹ̀rọ	[MPa]	550 - 1250	[psix10^3]	80 - 180
Iwọn otutu iṣẹ	Gbona	[ºC]	-196 / 600	[ºF]	-320.8 / 1112

Ibiti o

Awọn iwọn ila opin (min/max)	U.o.M.	Awọn iwọn ila opin (min/max)	U.o.M.	Awọn gilaasi pipe (ISO 3290-1 / DIN 5401 / AFBMA)**
0.300 - 300.000	[mm]	1/64 - 12	["]	G100-200-300-500-600-700-1000

Ipata Resistance

Idaabobo ipata ti o dara pupọ pẹlu ọwọ si awọn nkan Organic, resistance to dara si ọpọlọpọ awọn acids ti o lagbara (acetic, phosphoric, sulfuric acid) ati lori omi okun. Wọn ti tẹriba si pitting ati ipata crevice ni iwaju awọn ojutu kiloraidi gbona ati si ibajẹ ibajẹ nigbati iwọn otutu ba kọja 60°C. Wọn ko koju ni olubasọrọ pẹlu hydrochloric ati hydrofluoric acids, aqua regia, irin ati magnẹsia chlorides.