I-E36WA4 steel grade iyimikhiqizo egoqiwe eshisayo yezinsimbi zesakhiwo ezimweni zokulethwa kobuchwepheshe ezinokumelana nokugqwala okuthuthukisiwe komkhathi.Izakhi eziyinhloko ze-alloying i-chromium nickel nethusi ene-phosphorous eyengeziwe enikeza izimfanelo ezinhle kakhulu zokuzivikela. Njengoba insimbi iphendulana nezinto ezisemkhathini, i-material yakha ungqimba lokugqwala ngokuhamba kwesikhathi okuyinto empeleni evikela insimbi ekugqwaleni.
Insimbi ye-E36WA4 ingamabanga Alinganayo njengensimbi ye-S355J2WP (1.8946) ku-EN 10025 - 5: 2004 ejwayelekile kanye nensimbi ye-FE510D1K1 ku-UNI standard kanye ne-A242 Type1 yensimbi esezingeni le-ASTM.
Imininingwane:
Ubukhulu: 3mm-150mm
Ububanzi: 30mm-4000mm
Ubude: 1000mm--12000mm
Okujwayelekile: ASTM EN10025 JIS GB
I-E36WA4 Steel Chemical Composition
| C % | Mn % | Cr % | Si % | CEV % | S % |
| Ubukhulu 0.12 | Ubukhulu 1 | 0.3-1.25 | Ubukhulu 0.75 | Ubukhulu 0.52 | Ubukhulu 0.03 |
| Cu % | P % | ||||
| 0.25-0.55 | 0.06 - 0.15 |
| Ibanga | Okuncane. Yield Strength Mpa | I-Tensile Strength MPa | Umthelela | ||||||||
| E36WA4 | Ubukhulu Bezwi (mm) | Ubukhulu Bezwi (mm) | iziqu | J | |||||||
| Ubukhulu mm | ≤16 | >16 ≤40 |
>40 ≤63 |
> 63 ≤80 |
>80 ≤100 |
>100 ≤150 |
≤3 | >3 ≤100 | >100 ≤150 | -20 | 27 |
| E36WA4 | 355 | 345 | …. | …. | …. | …. | 510-680 | 470-630 | …. | ||
Uma izakhiwo zemishini ze-E36WA4 zishintshwe ngokuphawulekayo ngokubanda okuqinile, kungase kusetshenziswe ukudambisa ingcindezi noma ukwenziwa kwejwayelekile. Okujwayelekile kufanele futhi kusetshenziswe ngokulandela ukushisa okungaphandle kwebanga lokushisa elingu-750 - 1.050 °C nangemuva kokushisa ngokweqile. Amanani okuhlola okuqinile anikezwe kuthebula asebenza kumasampula e-longitudinal; uma kukhona umcu kanye nensimbi yeshidi lobubanzi obungu-≥600 mm asebenza kumasampuli aphambene.