42CrMo lembaran baja gulung panas/bar

42CrMo4 punika baja kanggo quenching lan tempering, kang wis kombinasi apik saka kekuatan lan kateguhan ing kahanan quenched lan tempered. Sawise quenching lenga, baja bakal liwat hardened nganti ø60 mm diameteripun bar. Struktur mikro kanthi ukuran sing luwih gedhe ora martensit kanthi lengkap. Baja ditrapake kanggo hardening induksi. Kekerasan lumahing bakal ngluwihi min. 53 HRC. 42CrMo4 bisa dikirim M-dianggep supaya ngoptimalake machinability.

Komposisi kimia
Kelas Baja	C	Si	Mn	P	S	Cr	Mo	Cu
35CrMo	0.38～0.45%	0.17～0.37%	0.50～0.80%	≤0,035%	≤0,035%	0.90～1.20%	0.15～0.25%	≤0,30%

Sifat mekanik

Kekuatan hasil σs/MPa (>=)	Kekuatan tarik σb/MPa (>=)	Elongation δ5/% (>=)	Pengurangan saka area ψ/% (>=)	Impact absorbing energy Aku2/J (>=)	Kekerasan HBS 100/3000 maks
≥930(95)	≥1080(110)	≥12	≥45	≥78(8)	≤217HB

Kanggo nambah umur die kanggo luwih saka 800.000 kaping mati, baja wis hardened bisa hardened dening quenching lan kurang suhu tempering. Nalika quenching, preheat ing 500-600 ℃ kanggo 2-4 jam, lan banjur tetep ing 850-880 ℃ kanggo wektu tartamtu (paling ora 2 jam), banjur sijine ing lenga lan kelangan kanggo 50-100 ℃ lan cooling online, atose bisa tekan 50 sawise quenching -52HRC, supaya kanggo nyegah cracking, 200 ℃ perawatan tempering suhu kurang kudu digawa metu langsung. Sawise tempering, atose bisa maintained ndhuwur 48HRC.

42CrMo Steel Heat Treatment

Annealing

Annealing ing 760 ± 10 ℃, tungku cooling kanggo 400 ℃ banjur online cooling.

Normalisasi

Normalisasi ing 760 ± 10 ℃, cooling online sawise metu saka pawon.

Cathetan Babagan Quenching lan Perawatan Tempering

Kudu mbayar manungsa waé kanggo suhu coolant Cairan. Lan kudu nggawe manawa ora ana kontaminasi lenga utawa impurities liyane. Yen ora, atose baja bakal ora cukup utawa metu saka imbangan.

Quenching lan tempering kanggo materi baja billet tanpa Processing, banjur bakal njaluk atose non-seragam. Dadi pangolahan forging utawa grinding perlu sadurunge Q + T.