AISI 4140 Baja Paduan

Baja Paduan AISI 4140 (UNS G41400)

Baja paduan ditunjuk kanthi nomer papat digit AISI lan kalebu macem-macem jinis baja, saben kanthi komposisi sing ngluwihi watesan B, C, Mn, Mo, Ni, Si, Cr, lan Va kanggo baja karbon.

Baja paduan AISI 4140 minangka baja paduan rendah kromium, molibdenum, lan mangan. Wis kekuatan lemes dhuwur, abrasion lan impact resistance, kateguhan, lan kekuatan torsional. Lembar data ing ngisor iki menehi ringkesan baja paduan AISI 4140.

AISI 4140 setara baja

negara	Cina	Jepang	Jerman	USA	Inggris
Standar	GB/T 3077	JIS G4105	DIN (W-Nr.) EN 10250	AISI/ASTM ASTM A29	BS 970
sasmita	42CrMo	SCM440	42crmo4/1.7225	4140	EN19/709M40

Komposisi kimia baja AISI 4140

sasmita	C	Si	Mn	P	S	Cr	Mo	Ni
42CrMo	0.38-0.45	0.17-0.37	0.5-0.80	≤0,035	≤0,035	0.9-1.2	0.15-0.25	-
SCM440	0.38-0.43	0.15-0.35	0.6-0.85	≤0,035	≤0.04	0.9-1.2	0.15-0.30	-
42crmo4/1.7225	0.38-0.45	≤ 0.4	0.6-0.9	≤0,025	≤0,035	0.9-1.2	0.15-0.30	-
4140	0.38-0.43	0.15-0.35	0.75-1.00	≤0,035	≤0.04	0.8-1.1	0.15-0.25	-
EN19/709M40	0.35-0.45	0.15-0.35	0.5-0.80	≤0,035	≤0,035	0.9-1.5	0.2-0.40	-

Sifat mekanik baja AISI 4140 (mung kanggo pandhuan)

sasmita	Kekuwatan tensile σb (MPa)	kekuatan ngasilaken σs (MPa)	Elongation δ5 (%)	Ngurangi ψ (%)	Nilai Dampak Akv (J)	Kekerasan
4140	≥1080	≥930	≥12	≥45	≥63	28-32HRC

Ringkesan baja AISI 4140

Ukuran	Babak	Dhiameter 6-1200 mm
	Plate/Flat/Blok	kekandelan 6mm-500mm
		Jembar 20mm-1000mm
perawatan panas	Normalisasi ; Annealed ; dipateni ; Tempered
Kondisi lumahing	Ireng; dikupas; polesan; Mesin; digiling; diuripake; giling
Kondisi pangiriman	Dipalsukan; Digulung panas; Digambar kadhemen
Tes	Kekuwatan tarik, kekuatan ngasilake, elongasi, area pengurangan, nilai impact, kekerasan, ukuran butir, tes ultrasonik, inspeksi AS, uji partikel magnetik, lsp.
Syarat-syarat pembayaran	T/T;L/C;/Dhuwit gram/ Paypal
Syarat dagang	FOB; CIF; C&F; lsp..
wektu pangiriman	30-45 dina
Aplikasi	AISI 4140 baja nemokake akeh aplikasi minangka forgings kanggo aerospace, lenga lan gas, automotive, tetanèn lan industri pertahanan etc. Aplikasi umum kanggo panggunaan baja 4140 kalebu: gigi palsu, kumparan, perlengkapan, jig, kerah, As, bagian conveyor, gagak, bagian logging, poros, sprocket, stud, pinion, poros pompa, ram, lan gear dering dll

Sifat Fisik

Sifat fisik baja paduan AISI 4140 disorot ing tabel ing ngisor iki.

Properti	Metrik	Imperial
Kapadhetan	7,85 g/cm3	0,284 lb/in³
Titik lebur	1416°C	2580°F

Sifat Mekanik

Tabel ing ngisor iki negesake sifat mekanik baja paduan AISI 4140.

Properti	Metrik	Imperial
Kekuwatan tensile	655 MPa	95000 psi
kekuatan ngasilaken	415 MPa	60200 psi
Bulk modulus (khas kanggo baja)	140 GPa	20300 ksi
Modulus geser (khas kanggo baja)	80 gpa	11600 ksi
Modulus elastis	190-210 GPa	27557-30458 ksi
rasio Poisson	0.27-0.30	0.27-0.30
Elongation ing break (ing 50 mm)	25.70%	25.70%
Hardness, Brinell	197	197
Kekerasan, Knoop (diowahi saka kekerasan Brinell)	219	219
Kekerasan, Rockwell B (diowahi saka kekerasan Brinell)	92	92
Kekerasan, Rockwell C (diowahi saka kekerasan Brinell. Nilai ing ngisor kisaran HRC normal, mung kanggo tujuan perbandingan)	13	13
Kekerasan, Vickers (diowahi saka kekerasan Brinell)	207	207
Machinability (adhedhasar AISI 1212 minangka 100 machinability)	65	65

Sifat termal

Sifat termal baja paduan AISI 4140 diwenehi ing tabel ing ngisor iki.

Properti	Metrik	Imperial
Koefisien ekspansi termal (@ 0-100°C/32-212°F)	12,2 µm/m°C	6,78 µin/in°F
Konduktivitas termal (@ 100°C)	42,6 W/mK	296 BTU ing/jam.ft².°F

Jeneng Liyane

Sebutan liyane sing padha karo baja paduan AISI 4140 kapacak ing tabel ing ngisor iki.

AMS 6349	ASTM A193 (B7, B7M)	ASTM A506 (4140)	ASTM A752 (4140)
AMS 6381	ASTM A194 (7,7M)	ASTM A513	ASTM A829
AMS 6382	ASTM A29 (4140)	ASTM A513 (4140)	SAE J1397 (4140)
AMS 6390	ASTM A320 (L7, L7M, L7D)	ASTM A519 (4140)	SAE J404 (4140)
AMS 6395	ASTM A322 (4140)	ASTM A646 (4140)	SAE J412 (4140)
AMS 6529	ASTM A331 (4140)	ASTM A711

Fabrikasi lan Perawatan Panas

Kemampuan mesin

Baja paduan AISI 4140 nduweni kemampuan mesin sing apik ing kondisi anil.

mbentuk

Baja paduan AISI 4140 nduweni daktilitas dhuwur. Bisa dibentuk kanthi nggunakake teknik konvensional ing kondisi anil. Mbutuhake tekanan utawa pasukan luwih akeh kanggo mbentuk amarga luwih angel tinimbang baja karbon biasa.

Welding

Baja paduan AISI 4140 bisa dilas kanthi nggunakake kabeh teknik konvensional. Nanging, sifat mekanik baja iki bakal kena pengaruh yen dilas ing kondisi sing diobati panas, lan perawatan panas pasca las kudu ditindakake.

Perawatan panas

AISI 4140 baja paduan digawe panas ing 845 ° C (1550 ° F) banjur quenching ing lenga. Sadurunge hardening, bisa dinormalisasi kanthi dipanasake ing 913 ° C (1675 ° F) kanggo wektu sing suwe, banjur didinginake hawa.

Forging

Baja paduan AISI 4140 ditempa ing 926 nganti 1205 ° C (1700 nganti 2200 ° F)

Panas Kerja

Baja paduan AISI 4140 bisa digarap panas ing 816 nganti 1038 ° C (1500 nganti 1900 ° F)

Kerja Dingin

Baja paduan AISI 4140 bisa digunakake kanthi adhem kanthi nggunakake cara konvensional ing kondisi anil.

Annealing

Baja paduan AISI 4140 dianil ing 872°C (1600°F) banjur dipendhem alon-alon ing tungku.

Tempering

Baja paduan AISI 4140 bisa digawe panas ing 205 nganti 649 ° C (400 nganti 1200 ° F) gumantung saka tingkat kekerasan sing dikarepake. Kekerasan baja bisa ditambah yen nduweni suhu tempering sing luwih murah. Contone, kekuatan tarik 225 ksi bisa digayuh kanthi tempering ing 316°C (600°F), lan kekuatan tarik 130 ksi bisa digayuh kanthi tempering ing 538°C (1000°F).

Hardening

AISI 4140 baja paduan bisa hardened dening karya kadhemen, utawa dadi panas lan quenching.