42CrMo wela olokaa pepa kila/bar

ʻO 42CrMo4 he kila no ka hoʻopauʻana a me ka hoʻouluʻana, kahi hui maikaʻi o ka ikaika a me ka paʻakikī i keʻano hoʻopiʻi a me ka huhū. Ma hope o ka hoʻopau ʻana i ka ʻaila, e hoʻopaʻa ʻia ke kila a hiki i ø60 mm bar ke anawaena. ʻAʻole martensite piha ka microstructure o nā ana nui. Pili ke kila i ka paakiki induction. E oi aku ka paakiki o ka ili i ka min. 53 HRC. Hiki ke hāʻawi ʻia ʻo 42CrMo4 i ka M-treated i mea e hoʻonui ai i ka machinability.

Hoʻohui Kimia
Papa kila	C	ʻO Si	ʻO Mn	P	S	Cr	Mo	Cu
35CrMo	0.38～0.45%	0.17～0.37%	0.50～0.80%	≤0.035%	≤0.035%	0.90～1.20%	0.15～0.25%	≤0.30%

Nā waiwai mīkini

Ka ikaika σs/MPa (>=)	Ka ikaika wili σb/MPa (>=)	ʻO ka lōʻihi δ5/% (>=)	Hoemi o ʻāpana ψ/% (>=)	Impact absorbing energy Aku2/J (>=)	Oolea HBS 100/3000 ka nui
≥930(95)	≥1080(110)	≥12	≥45	≥78(8)	≤217HB

I mea e hoʻonui ai i ke ola make i ʻoi aku ma mua o 800,000 mau manawa make, hiki ke hoʻopaʻa ʻia ke kila i hoʻopaʻa ʻia ma mua o ke kinai ʻana a me ka haʻahaʻa haʻahaʻa haʻahaʻa. Ke kinai, preheat ma 500-600 ℃ no 2-4 mau hola, a laila mālama ia ma 850-880 ℃ no kekahi manawa (ma ka liʻiliʻi o 2 mau hola), a laila e hoʻokomo i loko o ka aila a hoʻomaha i 50-100 ℃ a ʻO ka hoʻoluʻu ea, hiki i ka paʻakikī ke hiki i 50 ma hope o ke kinai ʻana -52HRC, i mea e pale ai i ka haki ʻana, 200 ℃ haʻahaʻa haʻahaʻa haʻahaʻa e hana koke ʻia. Ma hope o ka hoʻoulu ʻana, hiki ke mālama ʻia ka paʻakikī ma luna o 48HRC.

42CrMo kila wela wela

Hoʻopili

Hoʻopili i ka 760 ± 10 ℃, hoʻoluʻu i ka umu a hiki i 400 ℃ a laila hoʻoluʻu ea.

Hoʻoponopono maʻamau

Hoʻomaʻamaʻa ma 760 ± 10 ℃, hoʻoluʻu ea ma hope o waho o ka umu.

Nā memo e pili ana i ka Quenching and Tempering Treatment

Pono e hoʻolohe i ka mahana o ka wai coolant. A pono e hōʻoia i ka ʻole o ka ʻaila a i ʻole nā ​​mea haumia ʻē aʻe. A i ʻole, ʻaʻole lawa ka paʻakikī o ke kila a i ʻole ke kaulike.

ʻO ka Quenching a me ka hoʻomaʻamaʻa ʻana i nā mea kila billet me ka ʻole o ka hana ʻana, a laila e loaʻa ka paʻakikī like ʻole. No laila pono ka hana ʻana o ka forging a wili paha ma mua o ka Q+T.