20CrMnTi(H) hot rolled steel round bars
20CrMnTi(H) hot rolled steel round bars
20CrMnTi(H) hot rolled steel round bars
20CrMnTi(H) hot rolled steel round bars

20CrMnTi(H) hot rolled steel round bars

GB 20CrMnTi gear steel is GB standard Alloy Carburizing Gearing steel, GB 20CrMnTi properties is a chromium, manganese, titanium alloy steel specification. 20CrMnTi is equivalent with others standard bearing/Gearing steel, gearing steel
Product introduction
characteristics of hardened steel alloy tool steel, good carburizing heat treatment process and the performance of the steel at ≤960 ℃ fine grain structure, commonly used in long-term heating carburizing temperature, the grain grew no tendency little residual austenite after quenching, therefore, the steel has high strength and wear resistance, excellent cutting performance, the main performance and 20CrMnTi and 20CrNi steel similar. Tensile strength σ ≥1080MPa, yield strength σ ≥885MPa, elongation δ ≥10%, 45% reduction of swelling, impact toughness (impact toughness) α ≥69J / cm, hardness ≤207HB, blank sample size to 15mm.
Technical data
GB 20CrMnTi GB/T 3077 Mechanical

The mechanical properties of GB 20CrMnTi GB/T 3077 metals determine the range of usefulness of a material and establish the service life that can be expected. Mechanical properties are also used to help classify and identify material.

Rp0.2 (MPa)
Rm (MPa)
KV/Ku (J)
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
912 (≥) 863 (≥) 23 33 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 212
Physical performance parameters of GB 20CrMnTi GB/T 3077 are mainly indicated by density, poisson's ratio, thermal conductivity, specific thermal capacity, coefficient of thermal expansion, modulus of elasticity, electrical resistance value, etc.
Modulus of elasticity
Mean coefficient of thermal expansion 10-6/(°C)
between 20(°C) and
Thermal conductivity
Specific thermal capacity
Specific electrical resistivity
(Ω mm²/m)
Poisson’s coefficient, ν
24 - -     0.31 -  
956 121 - 12.3 423   -  
659 - 41 11.2     243 423

Heat treatment Related

  • Annealing of 20CrMnTi Alloy Gearing steel

Slowly heated to 790-810 ℃ and allow enough times, let the steel to be thoroughly heated, Then cool slowly in the furnace. Different annealing ways will get different hardness.The 20CrMnTi Gearing steel will get Hardness MAX 248 HB (Brinell hardness).

  • Quenching and temperature of 20CrMnTi gear steel

Heated slowly to 788°C, Then put in salt-bath furnace keep 1191 ℃to 1204 ℃。quenching by oil get 60 to 66 HRc hardness. High temperature tempering: 650-700℃,cool in air, get hardness 22 to 30HRC. Low temperature tempering: 150-200 ℃, Cool  in ari, get 61-66HRC hardness.

  • Hot work and cold work of 20CrMnTi Alloy Gearing steel

GB 20CrMnTi steel can hot worked at 205 to 538°C, 20CrMnTi Bearing/Gearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.

Related Products
W6Mo5Cr4V2(M2) hot rolled steel round bars
50Mn-60Mn hot rolled steel round bars
CM690 hot rolled steel round bars
40Cr hot rolled steel round bars
15CrMo hot rolled steel sheet
20Cr hot rolled steel sheet
35CrMo hot rolled steel sheet
20CrMo hot rolled steel sheet
12Cr1MoV hot rolled steel sheet
25Cr2MoVA hot rolled steel sheet
35CrMnSiA hot rolled steel sheet
30CrMnSiA Steel Round Bar
Q345E hot rolled steel sheet
Q345D hot rolled steel sheet
45# hot rolled steel sheet
Q345B hot rolled steel sheet
35# Steel Round Bar
20# hot rolled steel sheet
10# hot rolled round steel bar
T8-T10A hot rolled steel round bars
Q460D hot rolled steel round bars
40CrNiMo hot rolled steel round bars
42CrMo hot rolled steel sheet
GCr15 hot rolled steel round bars
60Si2Mn hot rolled steel round bars
27SiMn hot rolled steel round bars
30CrMnTi hot rolled steel round bars
20CrNiMo(8620H) hot rolled steel round bars
* Name
* E-mail
WhatsApp me