34CrNiMo6 hot rolled steel round bars
34CrNiMo6 hot rolled steel round bars
34CrNiMo6 hot rolled steel round bars
34CrNiMo6 hot rolled steel round bars

34CrNiMo6 hot rolled steel round bars

34CrNiMo6 is a quenching and tempering steel with high strength, high toughness and good hardenability. Used for large axles, machine components, tools and high strength fasteners. The steel can be induction hardened and it is weldable under certain conditions. Through hardenability to appr. 100 mm diameter bar with oil quenching.
34CrNiMo6 hot rolled steel round bars Application

EN DIN 34CrNiMo6 steel is used to make tools which demands good plasticity and high strength. It is usually selected to make the big size and important parts, such as heavy machinery axle,turbine shaft blade, high load of transmission parts, fasteners, crank shafts, gears, as well as heavily loaded parts for motor construction etc.

Gnee Steel is reliable to supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels. Please tell us your detailed requirements and have the best offer soon.

Chemical and Mechanical

34CrNiMo6 Chemical composition and Equivalents steel grade properties

BS EN 10083 – 3:2006 34CrNiMo6 C Si Si P S Cr Mo Ni
0.30-0.38 0.40 Max 0.50-0.80 0.025 max 0.035 max 1.30-1.70 0.15-0.30 1.30-1.70

34CrNiMo6 Steel Mechanical Properties       

Diameter(mm) < 16 16~ 40 40~100 100~160 160 ~250
Thickness t (mm) < 8 8~20 20~60 60~100 100~160
Tensile strength Rm (N/mm2) 1200 – 1400 1100 – 1300 1000 – 1200 900 – 1100 800 – 950
Elongation A (%) 9 min 10 Min 11 Min Min 12 13 Min
Reduction of area Z (%) 40Min 45 Min 50Min 55Min 55MIn
Toughness CVN (J) 35Min 45Min 45Min 45Min 45 Min
Yield strength Re (N/mm²) 1000 Min 900 Min 800 Min 700 Min 600 Min
 

EN 34CrNiMo6 Steel Standards And Equivalents

BS EN 10083 -3: 2006 34CrNiMo6 / 1.6582 ASTM A29: 2004 4337
BS EN 10250 – 3: 2000

3. EN/DIN 34CrNiMo6 Steel Chemical Composition Properties

BS EN 10083 – 3:2006 34CrNiMo6
/1.6582
C Mn Si P S Cr Mo Ni
0.30-0.38 0.5-0.8 0.40 max 0.025 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
BS EN 10250-3:2000 C Mn Si P S Cr Mo Ni
0.30-0.38 0.5-0.8 0.40 max 0.035 max 0.035 max 1.3-1.7 0.15-0.30 1.3-1.7
ASTM A29: 2004 4337 C Mn Si P S Cr Mo Ni
0.30-0.40 0.6-0.8 0.20-0.35 0.035 max 0.040 max 0.70-0.90 0.20-0.30 1.65-2.00

4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel

Properties < 16 >16 – 40 >40 – 100 >100 – 160 >160 – 250
Thickness t [mm] < 8 8<t<20 20<t<60 60<t<100 100<t<160
Yield strength Re [N/mm²] min. 1000 min. 900 min. 800 min. 700 min. 600
Tensile strength Rm [N/mm2] 1200 – 1400 1100 – 1300 1000 – 1200 900 – 1100 800 – 950
Elongation A [%] min. 9 min. 10 min. 11 min. 12 min. 13
Reduction of area Z [%] min. 40 min. 45 min. 50 min. 55 min. 55
Toughness CVN [J] min. 35 min. 45 min. 45 min. 45 min. 45

5.Heat Treatment of 34CrNiMo6 Engineering Steel

Quenched and Tempered (Q+T) of 34CrNiMo6 Steel

  • Heat 34CrNiMo6 round steel slowly to the temperature of 850°C;
  • Soak at this hardening temperature quench in oil;
  • Temper as soon as 34CrNiMo6 steels reach room temperature.
  • Heat uniformly to the suitable temperature;
  • Withdraw from the furnace and cool in the air.
  • The usual tempering temperature is 600°C which depending on the actual requirements.

6.Forging of DIN 34CrNiMo6 / 1.6582 Steel

Hot forming temperature: 1100-900oC.

7.Machinability of Steel 34CrNiMo6

Machining is best done with this 1.6582 alloy steel in the annealed or normalized and tempered condition. It can be machined by all conventional methods.

8.Welding

The alloy materials can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.

9.Application

EN DIN 34CrNiMo6 steel is used to make tools which demands good plasticity and high strength. It is usually selected to make the big size and important parts, such as heavy machinery axle,turbine shaft blade, high load of transmission parts, fasteners, crank shafts, gears, as well as heavily loaded parts for motor construction etc.

Gnee Steel is reliable to supply engineering 34CrNiMo6 steels / 1.6582 engineering alloy steels. Please tell us your detailed requirements and have the best offer soon.

Related Products
ASTM Steel Round Bars
Hot Sale Steel Round Bars
AISI 4140 Alloy Steel 1.7225 Steel,Scm440 Steel,42CrMo4 Steel,SAE4140 Steel,42CrMo Steel
AISI 4140 Steel 1.7225 42CrMo4 SCM440
5140 Steel Plate 1.7035 41Cr4 SCr440 Alloy Steel
 AISI 4340 Steel 36CrNiMo4 1.6511 EN24 817M40 SNCM439
AISI 8620 Steel
EN 34CrNiMo6 Steel
DIN 30CrNiMo8 steel
1.2083 Steel ,X42Cr13
W6Mo5Cr4V2Co5(M35)  hot rolled steel round bars
W18Cr4V hot rolled steel round bars
20CrNiMo(8620H) hot rolled steel round bars
Q390B-Q390D hot rolled steel round bars
CrWMn hot rolled steel round bars
3Cr2W8V hot rolled steel round bars
Cr12MoV hot rolled steel round bars
Cr12  hot rolled steel round bars
A105 hot rolled steel round bars
40CrMnMo Steel Round Bar
65Mn hot rolled steel round bars
16MnCr5 hot rolled steel round bars
B2 hot rolled steel round bars
38CrMoAl hot rolled steel round bars
18CrNiMo7-6
20MnCr5 hot rolled steel round bars
9SiCr hot rolled steel round bars
42CrMo hot rolled steel sheet
20CrMnMo
60Si2Mn hot rolled steel round bars
Inquiry
* Name
* E-mail
Phone
Country
Message