60Si2Mn uamea taai vevela lapotopoto pa

60Si2Mn tautotogo uʻamea o se silico-manganese puna uʻamea lautele faaaogaina ma sina malosi maualuga, elasticity ma hardenability nai lo 55Si2Mn. 60Si2Mn tautotogo alamanuia uʻamea maua mafolafola puna ma uta tele po o coil puna ma le lautele itiiti ifo i le 30mm. E fetaui lelei foi mo le faia o vaipuna e tete'e i le vevela ma le ala e le pala ma le vevela galue i lalo ole 250 °C ma fa'atasi ai ma le uta feliuliuai ma le mamafa maualuga. O puna vili taua tetele mo le galue i lalo, faʻapea foʻi ma masini faʻalavelave faʻafuaseʻi.

Vaega Vailaau:

C(%)	Si(%)	Mn(%)	P(%)	S(%)	Cr(%)	Ni(%)	Cu(%)	Fa'amama avega (Mpa)	Malosi fa'amalosi (Mpa)	Fa'aumi (%)
0.56-0.64	1.5-2.0	0.6-0.9	≦0.035	≦0.035	≦0.35	≦0.35	≦0.35	≧1175	≧1275	≧5

Mea fa'ainisinia:

Malosi fa'amalosi σb (MPa): ≥ 1274 (130)
Malosiaga σs (MPa): ≥1176 (120)
Fa'aumi δ10 (%): ≥5
Fa'aitiitia le vaega ψ (%): ≥25
Malosi: ta'avale vevela, ≤321HB; ata malulu + togafitiga vevela, ≤321HB

Fa'amatalaga vevela:

60Si2Mn togafitiga vevela faʻamatalaga: tineia 870 °C ± 20 ° C, suauʻu cooling; tempering 480 ° C ± 50 ° C (faapitoa manaʻomia, ± 30 ° C).
Fa'atonuga metallographic: fa'a'ita'i ita.

Tulaga tuʻuina atu: O loʻo tuʻuina atu le uʻamea vevela i totonu o le vevela poʻo le le faʻafefeteina o le vevela, ma o le uʻamea malulu e tuʻuina atu i le tulaga vevela.
Fa'amatalaga tu'uina atu ta'avale vevela: 2.0 ~ 18.0mm, fa'atasi ai ma le leai o se fa'ama'i. Fa'amatalaga tu'uina atu ta'avale malulu: 0.3~4.3mm (mea uamea)

Metotia togafitiga vevela

60Si2Mn auala togafitiga vevela o le isothermal tempering ma grading quenching, sub-vevela quenching ma maualuga vevela tempering, deformation faagasologa o togafitiga vevela. O le auala e mafai ona faʻaleleia lelei le malosi ma le ola tautua o le 60Si2Mn spring steel. 60Si2Mn o le tautotogo uamea, talafeagai mo le faia o le tautotogo laulaau taavale. 60Si2Mn tautotogo uʻamea vevela togafitiga isothermal tempering ma grading quenching, sub-vevela quenching ma maualuga vevela tempering, deformation faagasologa togafitiga vevela. O le auala e mafai ona faʻaleleia lelei le malosi ma le ola tautua o le 60Si2Mn spring steel.

mafiafia

60Si2Mn mafiafia o 7.85g / cm3. 60Si2Mn o loʻo faʻaaogaina lautele le silicon manganese spring steel, malosi, elasticity ma hardenability nai lo 55Si2Mn teisi maualuga. E talafeagai mo ta'avale nofoaafi, fale ta'avale ta'avale e maua ai se uta tele o vaipuna mafolafola po'o le lautele o le uaea o le 30mm i lalo ifo o le puna vili.