65Mn uamea o se Chinese GB tulaga tau puna uʻamea vasega, Manganese (Mn) faaleleia hardenability, o lea o le malosi, maaa, elasticity ma hardenability e maualuga atu nai lo le 65 # uamea, ae ua overheat lagona ma le ita brittleness. O le tineia o le vai e masani ona fai ma'eta'e. O le setete annealed e lelei machinability, palasitika deformation malulu maualalo, ma weldability le lelei.
65Mn maualuga carbon uʻamea e masani ona faʻaaogaina i le gaosiga o vaipuna mafolafola laiti vaega laiti, vaipuna lapotopoto, uati, ma isi.

Fa'asu'esu'ega o vaila'au

O le laulau o lo'o i lalo o lo'o lisiina ai le 65Mn maualuga kaponi fa'apipi'i vaila'au fa'atatau ile su'esu'ega vevela.

Tulaga Vailaau,%
Tulaga	Vasega	C	Si	Mn	P, ≤	S, ≤	Cr, ≤	Ni, ≤	Ku, ≤
GB/T 1222	65Mn	0.62-0.70	0.17-0.37	0.90-1.20	0.030	0.030	0.25	0.35	0.25

65Mn Meatotino Meatotino

Malosi: 7.85 g/cm3

		Meatotino Masini
Tulaga	Vasega	Malosi, MPa, ≥	Malosi e maua ai, MPa, ≥	Elongation, %, ≥	Fa'aitiitiga i le Eria, %, ≥	Brinell Malosi, HBW, ≤
GB/T 1222	65Mn	980	785	8.0	30	302

Fa'amatalaga: Fa'amau ma le lautele ma le umi o itu e le sili atu i le 80 mm ma u'amea mafolafola ma le mafiafia e le sili atu i le 40 mm.

Fa'amatalaga Togafitiga vevela

		Togafitiga vevela
Tulaga	Vasega	Tinei vevela, °C	Tineina mea	Fa'avevela vevela, °C
GB/T 1222	65Mn	830 ± 20	Suauu	540 ± 20

Faʻagasologa faʻafefe: Faʻafefeteina o le vevela (860 ± 10) °C, faʻasaoina o le vevela mo le 45-60min, faʻafefe o le ogaumu i le (750 ± 10) °C, faʻasaoina o le vevela mo le 3-3.5h, ma le ogaumu faʻamafanafana i le 650-660 °C, ona fa'alili i fafo o le ogaumu po'o le fa'amalo fa'agesegese i totonu o se lua fa'asao vevela.