EN DIN 34CrNiMo6 irin ni a lo lati ṣe awọn irinṣẹ eyiti o nilo ṣiṣu to dara ati agbara giga. Nigbagbogbo a yan lati ṣe iwọn nla ati awọn ẹya pataki, gẹgẹ bi axle ẹrọ ti o wuwo, abẹfẹlẹ ọpa turbine, ẹru giga ti awọn ẹya gbigbe, awọn ohun mimu, awọn ọpa crank, awọn jia, ati awọn ẹya ti o wuwo pupọ fun ikole mọto ati bẹbẹ lọ.
Gnee Steel jẹ igbẹkẹle lati pese awọn irin 34CrNiMo6 ina-ẹrọ / 1.6582 awọn irin alloy engineering. Jọwọ sọ fun wa awọn ibeere alaye rẹ ati ni ipese ti o dara julọ laipẹ.
| BS EN 10083 – 3:2006 | 34CrNiMo6 | C | Si | Si | P | S | Kr | Mo | Ni |
| 0.30-0.38 | 0.40 ti o pọju | 0.50-0.80 | ti o pọju 0.025 | ti o pọju 0.035 | 1.30-1.70 | 0.15-0.30 | 1.30-1.70 |
| Iwọn (mm) | < 16 | 16~ 40 | 40~100 | 100~160 | 160 ~250 |
| Sisanra t (mm) | < 8 | 8~20 | 20~60 | 60~100 | 100~160 |
| Agbara fifẹ Rm (N/mm2) | 1200 – 1400 | 1100 – 1300 | 1000 – 1200 | 900 – 1100 | 800 – 950 |
| Ilọsiwaju A (%) | 9 min | 10 min | 11 Min | Min 12 | 13 Min |
| Idinku agbegbe Z (%) | 40 min | 45 min | 50 min | 55 min | 55MIN |
| CVN lile (J) | 35 min | 45 min | 45 min | 45 min | 45 min |
| Agbara ikore Tun (N/mm²) | 1000 min | 900 min | 800 min | 700 min | 600 min |
Awọn ajohunše Irin EN 34CrNiMo6 Ati Awọn ibaramu
| BS EN 10083 -3: 2006 | 34CrNiMo6 / 1.6582 | ASTM A29: Ọdun 2004 | 4337 |
| BS EN 10250 – 3: 2000 |
3. EN /DIN 34CrNiMo6 Irin Kemikali Tiwqn Properties
| BS EN 10083 – 3:2006 | 34CrNiMo6 /1.6582 |
C | Mn | Si | P | S | Kr | Mo | Ni |
| 0.30-0.38 | 0.5-0.8 | 0.40 ti o pọju | ti o pọju 0.025 | ti o pọju 0.035 | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 | ||
| BS EN 10250-3: 2000 | C | Mn | Si | P | S | Kr | Mo | Ni | |
| 0.30-0.38 | 0.5-0.8 | 0.40 ti o pọju | ti o pọju 0.035 | ti o pọju 0.035 | 1.3-1.7 | 0.15-0.30 | 1.3-1.7 | ||
| ASTM A29: Ọdun 2004 | 4337 | C | Mn | Si | P | S | Kr | Mo | Ni |
| 0.30-0.40 | 0.6-0.8 | 0.20-0.35 | ti o pọju 0.035 | ti o pọju 0.040 | 0.70-0.90 | 0.20-0.30 | 1.65-2.00 |
4.Mechanical Properties of EN/DIN 34CrNiM06 / 1.6582 Alloy Steel
| Awọn ohun-ini | < 16 | > 16 – 40 | > 40 – 100 | > 100 - 160 | > 160 – 250 |
| Sisanra t [mm] | < 8 | 8| 20 | 60 | 100 | |
| Agbara ikore Tun [N/mm²] | min. 1000 | min. 900 | min. 800 | min. 700 | min. 600 |
| Agbara fifẹ Rm [N/mm2] | 1200 – 1400 | 1100 – 1300 | 1000 – 1200 | 900 – 1100 | 800 – 950 |
| Ilọsiwaju A [%] | min. 9 | min. 10 | min. 11 | min. 12 | min. 13 |
| Idinku agbegbe Z [%] | min. 40 | min. 45 | min. 50 | min. 55 | min. 55 |
| CVN lile [J] | min. 35 | min. 45 | min. 45 | min. 45 | min. 45 |
5.Heat Itoju ti 34CrNiMo6 Engineering Irin
Paná ati Ibinu (Q+T) ti 34CrNiMo6 Irin
6.Forging of DIN 34CrNiMo6 / 1.6582 Irin
Gbona lara otutu: 1100-900oC.
7.Machinability ti Irin 34CrNiMo6
Machining ti wa ni ti o dara ju ṣe pẹlu yi 1.6582 alloy irin ni annealed tabi deede ati tempered majemu. O le ṣe ẹrọ nipasẹ gbogbo awọn ọna aṣa.
8.Welding
Awọn ohun elo alloy le jẹ idapọ tabi resistance welded. Preheat ati post ooru weld ilana yẹ ki o wa ni atẹle nigba ti alurinmorin yi alloy nipa mulẹ ọna.
9.Ohun elo
EN DIN 34CrNiMo6 irin ni a lo lati ṣe awọn irinṣẹ eyiti o nilo ṣiṣu to dara ati agbara giga. Nigbagbogbo a yan lati ṣe iwọn nla ati awọn ẹya pataki, gẹgẹ bi axle ẹrọ ti o wuwo, abẹfẹlẹ ọpa turbine, ẹru giga ti awọn ẹya gbigbe, awọn ohun mimu, awọn ọpa crank, awọn jia, ati awọn ẹya ti o wuwo pupọ fun ikole mọto ati bẹbẹ lọ.
Gnee Steel jẹ igbẹkẹle lati pese awọn irin 34CrNiMo6 ina-ẹrọ / 1.6582 awọn irin alloy engineering. Jọwọ sọ fun wa awọn ibeere alaye rẹ ati ni ipese ti o dara julọ laipẹ.